Dual strategy of La3+ doping and carbon coating enhancing the rate performance of NaTi2(PO4)3 anode materials

Xiaojuan Liu,Zhifeng Li,Xiaohui Zhong,Chunxiang Wang,Sydorov Dmytro

DOI: https://doi.org/10.1007/s11581-024-05369-9

IF: 2.961

2024-01-10

Ionics

Abstract:NaTi 2 (PO 4 ) 3 (NTP) is considered a promising anode material for sodium-ion batteries due to its open and stable framework structure. However, its poor conductivity prevents its direct application as an anode material. In this paper, a dual strategy of La 3+ doping and carbon coating is proposed to improve the conductivity of NTP. The results show that the NTP-La 0.06 @C electrode doped with 6.00% La and 5.00 wt% of carbon coating has excellent electrochemical performance, and the coulombic efficiency is up to 95.31% in the first cycle. The initial specific capacity is 103.05 mAh·g −1 with a capacity retention of 97.30% after 1000 cycles at 10C rate. Even after 2000 cycles, there is still a specific capacity of 98.62 mAh·g −1 with a capacity retention of 92.71%, and as well as the NTP-La 0.06 @C has a higher Na + -insert diffusion coefficient of 3.19×10 −11 cm 2 ·s −1 than the pristine NTP@C of 2.35×10 −11 cm 2 ·s −1 during charging. Therefore, the La 3+ doping and carbon coating strategy shows great potential in improving the performance of NaTi 2 (PO 4 ) 3 anode materials.

chemistry, physical,physics, condensed matter,electrochemistry