Crystal doping of K ion on Na site raises the electrochemical performance of NaTi2(PO4)3/C anode for sodium-ion battery

Na Liu,Zhangxing He,Jing Zhu,Lei Dai,Yuehua Li,Wei Meng,Ling Wang

DOI: https://doi.org/10.1007/s11581-020-03468-x

IF: 2.961

2020-01-28

Ionics

Abstract:<p class="a-plus-plus">Sodium-ion battery is a rocking chair battery similar to lithium-ion battery and is considered to have a promising future due to low cost and extensive resources. As anode for sodium-ion battery, NaTi<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub> has attracted lots of attention due to its thermal stability and three-dimensional channels. In this work, we employed crystal doping of K ion on Na site to raise electrochemical performance of NaTi<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>/C composites. NaTi<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>/C doped with K was synthesized and used as anode for sodium-ion battery. XRD and SEM results imply that introduction of K ion has no significant change in the main crystal form and morphology of materials. Among Na<sub class="a-plus-plus">1-x</sub>K<sub class="a-plus-plus">x</sub>Ti<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>/C (<em class="a-plus-plus">x</em> = 0, 0.01, 0.03, 0.05) composites, Na<sub class="a-plus-plus">0.97</sub>K<sub class="a-plus-plus">0.03</sub>Ti<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>/C (NC/K-3) shows the best rate property, outstanding cycling performance, and the lowest charge transfer resistance. It delivers capacities of 206.65, 139.14, and 94.45 mAh g<sup class="a-plus-plus">−1</sup> at 0.1, 1.2, and 3 A g<sup class="a-plus-plus">−1</sup>, severally. Besides, even after 1000 cycles at 1.2 A g<sup class="a-plus-plus">−1</sup>, NC/K-3 keeps the discharge capacity at 89.5 mAh g<sup class="a-plus-plus">−1</sup> and 39.2 mAh g<sup class="a-plus-plus">−1</sup> higher than that of bare NaTi<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>/C. In conclusion, K doping on Na site by sol-gel route is a viable modification method to improve performance of NaTi<sub class="a-plus-plus">2</sub>(PO<sub class="a-plus-plus">4</sub>)<sub class="a-plus-plus">3</sub>/C composite as anode for sodium-ion batteries.</p>

chemistry, physical,physics, condensed matter,electrochemistry