Separation and recovery of copper in Cu−As-bearing copper electrorefining black slime by oxidation acid leaching and sulfide precipitation

Mei-qing SHI,Xiao-bo MIN,Chen SHEN,Li-yuan CHAI,Yong KE,Xu YAN,Yan-jie LIANG

DOI: https://doi.org/10.1016/s1003-6326(21)65564-4

IF: 3.752

2021-04-01

Transactions of Nonferrous Metals Society of China

Abstract:A new hydrometallurgical route for separation and recovery of Cu from Cu−As-bearing copper electro- refining black slime was developed. The proposed process comprised oxidation acid leaching of Cu−As-bearing slime and selective sulfide precipitation of Cu from the leachate. The effects of various process parameters on the leaching and precipitation of Cu and As were investigated. At the first stage, Cu extraction of 95.2% and As extraction of 97.6% were obtained at 80 °C after 4 h with initial H2SO4 concentration of 1.0 mol/L and liquid-to-solid ratio of 10 mL/g. In addition, the leaching kinetics of Cu and As was successfully reproduced by the Avrami model, and the apparent activation energies were found to be 33.6 and 35.1 kJ/mol for the Cu and As leaching reaction, respectively, suggesting a combination of chemical reaction and diffusion control. During the selective sulfide precipitation, about 99.4% Cu was recovered as CuS, while only 0.1% As was precipitated under the optimal conditions using sulfide-to-copper ratio of 2.4:1, time of 1.5 h and temperature of 25 °C.

metallurgy & metallurgical engineering