Abstract:Understanding field failure and degradation modes in solar photovoltaic (PV) modules is very important for various reasons especially for this widely used technology. The University of Applied Sciences Ostwestfalen-Lippe in Höxter owns photovoltaic-modules of different cell types, sizes and operation periods in German weather conditions. This paper presents a detailed degradation investigation and performance parameters analysis for chosen samples of polycrystalline, monocrystalline and thin film modules in the laboratory and outdoor test conditions after 10 years of exposure. The obtained measurements were standardized and then compared with the warranted values of the manufacturer’s datasheets for each module type. The real outdoor measurements for the larger units show that the maximum power Pmax after 10 years of exposure for polycrystalline, monocrystalline and amorphous thin film modules had declined by: 8.47%, 37.67%, and 19.05% respectively, which translates to an annual linear degradation rates of 0.652%, 3.67%, and 1.465% for each type respectively. While the maximum power output of the smaller units had declined by 19.05%, 19.36%, and 21.75% for polycrystalline, monocrystalline and amorphous thin film modules respectively, which also translated to annual linear degradation rates of 1.48%, 1.67%, and 0.6% for each type respectively. On the other hand, the laboratory tests for these modules show that there is a clear variation with the obtained outdoor results, where the Pmax for the same larger units had declined by 39.6%, 57.4%, and 82.5% for polycrystalline, monocrystalline and thin film modules respectively, While the Pmax output of smaller units had declined by 51.2%, 39.38%, and 9.39% for polycrystalline, monocrystalline and thin film modules respectively, The comparison of the efficiency and fill factor parameters for the obtained results with the manufacturer’s data shows that the outdoor measurements introduce close results than the laboratory results. The discoloration of the encapsulant is the most frequently occurring visually observable defects on the modules.

Assessing Field Degradation of PV Modules by Near‐Infrared Absorption Spectroscopy of Ethylene Vinyl Acetate Encapsulant

Degradation analysis of field-exposed photovoltaic modules with non-fluoropolymer-based backsheets

PV Modules and Their Backsheets -- A Case Study of a Multi-MW PV Power Station

From performance measurements to molecular level characterization: Exploring the differences between UV and DH weathering of PV modules

Early‐stage identification of encapsulants photobleaching and discoloration in crystalline silicon photovoltaic module laminates

Nondestructive Estimation of Strength Deterioration in Photovoltaic Backsheets Using a Portable Near Infrared Spectrometer

Non-Destructive Failure Detection and Visualization of Artificially and Naturally Aged PV Modules

Impact of environmental variables on the degradation of photovoltaic components and perspectives for the reliability assessment methodology

XPS analysis of damp heat aged and fractured polymer/glass laminates

Comparison of Degradation Behavior of Newly Developed Encapsulation Materials for Photovoltaic Applications under Different Artificial Ageing Tests

Material characterization of seven photovoltaic backsheets using seven accelerated test conditions

Differential degradation patterns of photovoltaic backsheets at the array level

Investigation on the Effect of Accumulated Charge-Induced Degradation on Multilayer Photovoltaic Insulating Backsheets Based on Atomic Force Microscopy

A Comparative Investigation on Outdoor and Laboratory Test of the Degradation Rates for Different Types of Photovoltaic Modules with Different Exposure Periods

Nanoindentation Reveals Crosslinking Behavior of Solar Encapsulants—The Methodological Advantages over Bulk Methods

Lifetime Evaluation of Photovoltaic Polymeric Backsheets under Ultraviolet Radiation: From Chemical Properties to Mechanical Modeling

Aging behavior and degradation of different backsheets used in the field under various climates in China

Properties and degradation behaviour of polyolefin encapsulants for photovoltaic modules

First principles modeling of polymer encapsulant degradation in Si photovoltaic modules

Enhancing photovoltaic modules encapsulation: Optimizing lamination processes for Polyolefin Elastomers (POE) through crosslinking behavior analysis

Assessment of the energy recovery potential of waste Photovoltaic (PV) modules