Inspired by placoid scale to fabricate MXene derivative biomimetic structure on the improvement of interfacial compatibility, mechanical property, and fire safety of epoxy nanocomposites
Zhenting Yin,Bibo Wang,Qinbo Tang,Jingyi Lu,Can Liao,Pengfei Jia,Liang Cheng,Lei Song
DOI: https://doi.org/10.1016/j.cej.2021.133489
IF: 15.1
2022-03-01
Chemical Engineering Journal
Abstract:In recent years, developing high performance thermosetting nanocomposites has attracted wide-ranging research attention. As a rising two-dimensional material, MXene still confront the intrinsic weakness for preparing epoxy resin with superior comprehensive performance. Inspired by the overlap architecture of placoid scale, an in-situ growth technique was applied to fabricate biomimetic-structural MXene derivative, which displayed significant increase in interfacial compatibility, mechanical property, and flame retardancy of epoxy resin (EP). In contrast to pure EP, the tensile strength and impact strength of EP nanocomposites increased by 30.1% and 43.5%, respectively. Furthermore, the fire hazard of EP nanocomposites was significantly reduced. With 5 wt% of PEPA-IPTS@Ti3C2Tx incorporated into EP (EP5), the peak of total heat release (THR) and total smoke production (TSP) decreased by 44.1% and 26.8%, respectively. Therefore, biomimetic structure nanohybrid (PEPA-IPTS@Ti3C2Tx) provides a facile and reliable strategy to prepare EP nanocomposites with excellent comprehensive performances.
engineering, chemical, environmental