Wear Behavior of TiAlVN-Coated Tools in Milling Operations of INCONEL® 718

Naiara P. V. Sebbe,Filipe Fernandes,Franciso J. G. Silva,André F. V. Pedroso,Rita C. M. Sales-Contini,Marta L. S. Barbosa,Luis M. Durão,Luis L. Magalhães

DOI: https://doi.org/10.3390/coatings14030311

IF: 3.236

2024-03-04

Coatings

Abstract:The use of coatings on cutting tools offers several advantages from the point of view of wear resistance. A recent technique with great coating deposition potential is PVD HiPIMS. TiAlN-based coatings have good resistance to oxidation due to the oxide layer that is formed on their surface. However, by adding doping elements such as Vanadium, it is expected that the wear resistance will be improved, as well as its adhesion to the substrate surface. INCONEL® 718 is a nickel superalloy with superior mechanical properties, which makes it a difficult-to-machine material. Milling, due to its flexibility, is the most suitable technique for machining this alloy. Based on this, in this work, the influence of milling parameters, such as cutting speed (Vc), feed per tooth (fz), and cutting length (Lcut), on the surface integrity and wear resistance of TiAlVN-coated tools in the milling of INCONEL® 718 was evaluated. The cutting length has a great influence on the process, with the main wear mechanisms being material adhesion, abrasion, and coating delamination. Furthermore, it was noted that delamination occurred due to low adhesion of the film to the substrate, as well as low resistance to crack propagation. It was also observed that using a higher cutting speed resulted in increased wear. Moreover, in general, by increasing the milling parameters, machined surface roughness also increased.

materials science, multidisciplinary,physics, applied, coatings & films

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to explore the wear behavior of TiAlVN - coated tools during milling INCONEL® 718 and its influencing factors. Specifically, the research aims to evaluate the effects of different milling parameters (such as cutting speed \( V_c \), feed per tooth \( f_z \) and cutting length \( L_{cut} \)) on the surface integrity and wear resistance of TiAlVN - coated tools.

### Specific background and challenges of the problem

1. **Material properties**:
- INCONEL® 718 is a nickel - based superalloy with excellent mechanical properties, which also makes it a difficult - to - machine material.
- The TiAlVN coating is deposited on the cutting tool by the PVD HiPIMS process, aiming to improve its wear resistance and adhesion to the substrate.

2. **Machining difficulties**:
- Milling is the most commonly used technique for machining this alloy because it is flexible and can produce good surface finish.
- During the milling process, the main wear mechanisms include material adhesion, abrasive wear and coating spalling.

3. **Research objectives**:
- Evaluate the effects of different milling parameters on the surface integrity and wear resistance of TiAlVN - coated tools.
- Analyze the influence of cutting length on the machining process, especially how it causes coating spalling and crack propagation.
- Investigate whether a higher cutting speed will lead to greater wear.
- Explore whether increasing milling parameters will increase the roughness of the machined surface.

### Research methods

To achieve the above - mentioned goals, the researchers carried out the following work:

1. **Experimental design**:
- Conduct helical milling experiments using cemented carbide tools with TiAlVN coating.
- Vary different milling parameters (cutting speed, feed per tooth and cutting length), and test with three tools under each condition.

2. **Surface roughness analysis**:
- Measure the roughness of the machined surface using a Mahr Perthometer M2 profilometer and evaluate it according to the DIN EN ISO 4288:1996 standard.

3. **Tool wear analysis**:
- Analyze the tool wear using a scanning electron microscope (SEM) and an energy - dispersive X - ray spectroscopy (EDS) system.
- Select the VB3 position for wear measurement according to the ISO 8688 - 2:1986 standard and record the wear data under different conditions.

Through these studies, the authors hope to fill the research gap in the literature regarding the wear behavior of TiAlVN - coated tools when milling INCONEL® 718 and provide a scientific basis for optimizing machining parameters.