Investigations on the Surface Integrity and Wear Mechanisms of TiAlYN-Coated Tools in Inconel 718 Milling Operations

Francisco J. G. Silva,Naiara P. V. Sebbe,Rúben D. F. S. Costa,André F. V. Pedroso,Rita C. M. Sales-Contini,Marta L. S. Barbosa,Rui P. Martinho
DOI: https://doi.org/10.3390/ma17020443
IF: 3.4
2024-01-18
Materials
Abstract:Inconel 718 is a Ni superalloy with superior mechanical properties, even at high temperatures. However, due to its high hardness and low thermal conductivity, it is considered a difficult-to-machine material. This material is widely used in applications that require good dimensional stability, making the milling process the most used in machining this alloy. The wear resulting from this process and the quality of the machined surface are still challenging factors when it comes to Inconel 718. TiAlN-based coating has been used on cutting tools with Yttrium as a doping element to improve the process performance. Based on this, this work evaluated the machined surface integrity and wear resistance of cutting tools coated using Physical Vapor Deposition (PVD) HiPIMS with TiAlYN in the end milling of Inconel 718, varying the process parameters such as cutting speed (vc), feed per tooth (fz), and cutting length (Lcut). It was verified that the Lcut is the parameter that exerts the most significant influence since, even at small distances, Inconel 718 already generates high tool wear (TW). Furthermore, the main wear mechanisms were abrasive and adhesive wear, with the development of a built-up edge (BUE) under a125 m/min feed rate (f) and a Lcut = 15 m. Chipping, cracking, and delamination of the coating were also observed, indicating a lack of adhesion between the coating and the substrate, suggesting the need for a good interlayer or the adjustment of the PVD parameters.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is **to improve the tool life and surface quality during the milling process of Inconel 718 material**. Specifically, the research focuses on: 1. **The influence of tool coatings on wear**: By using TiAlYN coatings (deposited by PVD HiPIMS technology), evaluate its influence on the tool wear behavior under different cutting parameters. The TiAlYN coating is selected because of its high hardness and good thermal stability, and yttrium (Yttrium) is added as a doping element to further improve the mechanical properties and antioxidant capacity of the coating. 2. **Optimization of surface integrity**: Study the influence of different cutting parameters (such as cutting speed \( v_c \), feed per tooth \( f_z \) and cutting length \( L_{\text{cut}} \)) on the machined surface roughness (SR) to find the best processing conditions, so as to obtain better surface quality and higher production efficiency. 3. **Analysis of wear mechanisms**: Through scanning electron microscopy (SEM) and energy - dispersive spectroscopy (EDS) techniques, analyze the tool wear phenomena in detail, identify the main wear mechanisms (such as abrasive wear, adhesive wear, edge chipping, etc.), and explore the relationships between these wear mechanisms and processing parameters. 4. **Optimization of process parameters**: By comparing the experimental results under different cutting parameters, determine the optimal combination of processing parameters to reduce tool wear, improve tool life, and ensure high - quality machined surfaces. In summary, this research aims to improve the surface integrity and tool life of Inconel 718 material in milling by optimizing the performance of TiAlYN coatings and processing parameters, thereby improving processing efficiency and product quality.