Abstract:The nickel(Ni)-patterned electrode enables researchers to quantify the triple-phase boundary (TPB) length and Ni surface area, exclude the influence of bulk gas diffusion and clearly separate the active regions of the chemical/electrochemical reactions. This tool has been studied for identifying the reaction mechanism in SOFC but rarely in SOEC. In this study, the Ni-patterned electrodes with the stripe width of 100 μm were tested in both the solid oxide fuel cell (SOFC) and solid oxide electrolysis cell (SOEC) modes at the atmosphere of H2O/H2 and further H2O/CO2/H2/CO. The experimental test shows the stability of the Ni-patterned electrode in the H2O/H2 atmosphere was much poorer than that in the CO/CO2 atmosphere due to the nickel reacting with steam. Thus, the Ni-patterned electrode needed to operate at a temperature of ≤700oC with the inlet H2/H2O molar ratio of >7 and the current-applied time shouldn’t be over 5 h to keep the accuracy of the TPB length and Ni surface area. The effects of the temperature, partial pressure of H2O and H2 are investigated. The activation energy of the Ni-patterned electrodes was 0.386 eV. The electrochemical performance had a positive correlation with both the partial pressure of H2 and H2O, especially showed higher sensitivity to the partial pressure of H2O. Further, a possible mechanism of the H2O/H2 electrochemical conversion was proposed according to the experimental data and existing literature, which contains two-step charge-transfer reaction: H(Ni)+O2-(YSZ)OH-(YSZ)+(Ni)+e- and H(Ni)+OH-(YSZ)H2O(YSZ)+(Ni)+e-. Based on the experiments, an analytical calculation was performed to investigate the rate-determining steps in the Ni-patterned electrodes by bridging the connection between the kinetic parameters and operating conditions. The results indicate the rate-limiting steps may be different for the SOFC and SOEC modes. In SOFC mode, the H2 electrochemical oxidation could depend more on the charge-transfer reaction H(Ni)+O2-(YSZ)→OH-(YSZ)+(Ni)+e-, however in SOEC mode, the rate-determining step of the H2O electrochemical reduction should be H2O(YSZ)+(Ni)+e-→OH-(YSZ)+H(Ni). In this way, a reversible mechanism could be applied for reversible SOFC (RSOFC) to describe the conversion between hydrogen and steam by different charge-transfer-reaction domination in the SOFC and SOEC mode. Figure 1

Electrolysis of carbon dioxide in Solid Oxide Electrolysis Cells

Oxidation Process of Ni Cathode in CO2 Electrolysis in SOEC: X-Ray and DFT Study

Carbon Monoxide/carbon Dioxide Electrochemical Conversion on Patterned Nickel Electrodes Operating in Fuel Cell and Electrolysis Cell Modes

Pure CO2 electrolysis over an Ni/YSZ cathode in a solid oxide electrolysis cell

Different Performance and Mechanisms of CO2 Electrolysis with CO and H2 As Protective Gases in Solid Oxide Electrolysis Cell

Durable SOC stacks for production of hydrogen and synthesis gas by high temperature electrolysis

Mechanism for Reversible CO/CO2 Electrochemical Conversion on a Patterned Nickel Electrode

Electrochemical characteristics of patterned nickel electrodes on single-crystal YSZ in CO/CO2 atmospheres for operating in fuel cell/electrolysis cell modes

Ni-cermet with straight pore paths as cathode for solid oxide electrolysis cell enabling energy-efficient and coking-resistant conversion of CO2

Highly efficient, coke-free electrolysis of dry CO 2 in solid oxide electrolysis cells

Performance and Methane Production Characteristics of H2O–CO2 Co-Electrolysis in Solid Oxide Electrolysis Cells

Carbon Deposition on Patterned Nickel/yttria Stabilized Zirconia Electrodes for Solid Oxide Fuel Cell/solid Oxide Electrolysis Cell Modes

Simultaneous Electrochemical Reduction of Carbon Dioxide and Partial Oxidation of Methane in a Solid Oxide Cell with Silver-Based Cathode and Nickel-Based Anode

Energy Storage and Syngas Production by Switching Cathode Gas in Nickel-Yttria Stabilized Zirconia Supported Solid Oxide Cell

Enhancing Electrochemical Efficiency of Solid Oxide Electrolysis Cells for Carbon Dioxide Reduction Through Nickel‐Doped Titanate‐Based Cathode with Doped Ceria Electrolyte

Electrochemical Characterization and Mechanism Analysis of High Temperature Co-electrolysis of CO2 and H2O in a Solid Oxide Electrolysis Cell

Reaction Mechanism and Rate-Determining Step Speculation of Reversible CO/CO2 Electrochemical Conversion on the Nickel Patterned Electrodes

Metal-supported solid oxide electrolysis cell for direct CO2 electrolysis using stainless steel based cathode

A Highly-Performed, Dual-Layered Cathode Supported Solid Oxide Electrolysis Cell for Efficient CO2Electrolysis Fabricated by Phase Inversion Co-Tape Casting Method

Selective high-temperature CO2 electrolysis enabled by oxidized carbon intermediates

Engineering dual-exsolution on self-assembled cathode to achieve efficient electrocatalytic CO 2 reduction