Abstract:Multi-material Laser Beam Powder Bed Fusion (PBF-LB) is a promising approach to meet industrial demands for multifunctional components, due to its enhanced freedom of design. Copper and stainless steel are interesting materials to be combined due to the high electrical and thermal conductivity of copper and the mechanical strength and wear resistance of steel. However, this system suffers from copper contamination cracking (CCC), a phenomenon which leads to intergranular cracking of the steel due to penetration of liquid copper. The more these materials intermix, the greater the amount of copper that can penetrate and damage the steel. Mixing is more intense when steel is below copper during printing, a situation that cannot always be avoided due to design constraints. In this sense, this research tackles the worst scenario of printing CuCrZr onto 316 L and analyses the effect of beam shaping on interface quality. For the first time, a ring-mode laser was applied to multi-material PBF-LB with the goal to reduce intermixing. It was observed that using a ring-mode laser source instead of a Gaussian beam decreases mixing of the two alloys and reduces interface defects, albeit being unable to completely suppress cracking. Grain size and texture were also affected by the beam shape, with the Gaussian beam leading to formation of small equiaxed grains along 20 layers of CuCrZr, resulting in random texture. The ring-mode laser source, on the other hand, yields columnar grains and texture along the build direction. Both beam shapes were observed to induce supercooling below the liquid miscibility gap in the Cu–Fe system. Besides the expected γ-Fe and ε-Cu phases, iron was also found to crystallize in a body-centered cubic (BCC) lattice structure, which is believed to happen due to Ni depletion of the steel in Cu-rich compositions, coupled to insufficient copper within the Fe-rich liquid during solidification. BCC fractions are higher for the Gaussian beam. These differences in microstructure and BCC fraction are attributed to the high intermixing of CuCrZr and 316 L when applying Gaussian beams, which is around 10 times higher than with the ring-mode laser.

Towards manufacturing intra-layer multi-material mould tools with vertical interfaces using laser-based powder bed fusion

Laser powder bed fusion of 316L stainless steel and K220 copper multi-material

Evaluation of material extrusion and laser-assisted in situ consolidation integrated additive manufacturing for multi-material components

Understanding of process and material behaviours in additive manufacturing of Invar36/Cu10Sn multiple material components via laser-based powder bed fusion

A Facile and Sustainable Integrated Fabrication Strategy for Multi-Performance 316l Stainless Steel

Additive Manufacturing of Horizontal and 3D Functionally Graded 316L/Cu10Sn Components via Multiple Material Selective Laser Melting

Microstructural Control of a Multi‐Phase PH Steel Printed with Laser Powder Bed Fusion

Novel strategy for automated quality enhancement of up-facing inclined surfaces by incremental dual laser powder bed fusion

Recent progress on additive manufacturing of multi-material structures with laser powder bed fusion

Development and characterisation of direct laser sintering Cu-based metal powder

Additive manufacturing of Ti–6Al–4V/Al–Cu–Mg multi-material structures with a Cu interlayer

The impact of interfacial characteristics on the interfacial properties of 316 L/CuSn10 multi-material manufactured by laser powder bed fusion

Selective laser powder bed fusion for manufacturing of 3D metal-ceramic multi-materials assemblies

Effect of interface-layer process parameters on forming quality of 316L/CuSn10 bimetals fabricated via laser powder bed fusion

Fabricating Inner Channels in Laser Additive Manufacturing Process Via Thin-Plate-Preplacing Method.

Recent progress and scientific challenges in multi-material additive manufacturing via laser-based powder bed fusion

Laser Fusion of Powder and Foil – a Multi Material Approach to Additive Manufacturing

The interplay of local chemistry and plasticity in controlling microstructure formation during laser powder bed fusion of metals

Concurrent modeling of porosity and microstructure in multilayer three-dimensional simulations of powder-bed fusion additive manufacturing of INCONEL 718

Dynamics of pore formation during laser powder bed fusion additive manufacturing

Effects of beam shaping on copper-steel interfaces in Multi-material Laser Beam Powder Bed Fusion