Low-temperature dissociation of CO 2 molecules on vicinal Cu surfaces

Takanori Koitaya,Yuichiro Shiozawa,Yuki Yoshikura,Kozo Mukai,Shinya Yoshimoto,Jun Yoshinobu

DOI: https://doi.org/10.1039/d3cp06336d

IF: 3.3

2024-03-08

Physical Chemistry Chemical Physics

Abstract:The reaction of carbon dioxide on the vicinal Cu surfaces at low temperatures was investigated by infrared reflection absorption spectroscopy, scanning tunneling microscopy, X-ray photoelectron spectroscopy, and quadrupole mass spectrometry. Dissociation of CO 2 molecules into CO on the Cu(997) and Cu(977) surfaces was observed at temperatures between 80 K and 90 K, whereas it did not occur on Cu(111) under a similar condition. CO and physisorbed CO 2 were the main adsorbates during the reaction. In contrast, the amount of atomic oxygen on the surface was small. The dissociation of CO 2 was promoted by the small amount of oxygen produced by the CO 2 dissociation on the Cu surfaces. This leads to the induction period in the CO 2 reaction; the initial reaction rate on the clean Cu surfaces was low, and the coadsorbed oxygen enhanced the dissociation reactivity of CO 2 . Mass analysis of desorption species during the reaction revealed that the observed CO formation on the vicinal Cu surface is mainly caused by an oxygen-exchange reaction with residual CO in an ultra-high vacuum chamber.

chemistry, physical,physics, atomic, molecular & chemical

What problem does this paper attempt to address?

The paper aims to study the reaction mechanism of carbon dioxide (CO₂) on copper (Cu) surfaces under low-temperature conditions, specifically exploring the dissociation behavior of CO₂ on copper surfaces with stepped structures. Specifically, the paper focuses on the following aspects:

1. **Experimental Conditions**:
- The study was conducted under ultra-high vacuum (UHV) conditions using techniques such as Infrared Reflection Absorption Spectroscopy (IRAS), X-ray Photoelectron Spectroscopy (XPS), Quadrupole Mass Spectrometry (QMS), and Scanning Tunneling Microscopy (STM).
- The experiments were performed at low temperatures (approximately 80 to 90 K).

2. **Main Findings**:
- It was found that CO₂ molecules can dissociate into CO on Cu(997) and Cu(977) surfaces, whereas dissociation does not occur on the flat Cu(111) surface.
- The dissociation process is accompanied by the generation of a small amount of oxygen atoms, which promote subsequent CO₂ dissociation reactions.
- There is an induction period for CO₂ dissociation, meaning that the initial reaction rate on a clean Cu surface is relatively low, but the dissociation rate gradually increases with reaction time.

3. **Mechanism Exploration**:
- The study indicates that the observed CO₂ dissociation on Cu(997) and Cu(977) surfaces is primarily achieved through an oxygen exchange reaction between CO and background CO.
- Pre-adsorbing a small amount of oxygen can significantly promote the CO₂ dissociation reaction, while an excess of oxygen can inhibit dissociation or hinder the diffusion of products.

4. **Comparison with Other Conditions**:
- The paper also discusses the dissociation behavior of CO₂ on Cu surfaces under near-atmospheric pressure (NAP) conditions, finding that at higher temperatures (e.g., 300 K), CO₂ can dissociate into CO, O, and CO₃, with a higher oxygen coverage.
- Under UHV conditions, the oxygen coverage is very low (less than 0.03 ML), whereas under NAP conditions, the oxygen coverage is higher.

In summary, the paper reveals the dissociation mechanism of CO₂ on copper surfaces with stepped structures under low-temperature conditions through various experimental methods and explores the changes in dissociation behavior under different conditions.