Use of Hydrogel Electrolyte in Zn-MnO2 Rechargeable Batteries: Characterization of Safety, Performance, and Cu2+ Ion Diffusion

Jungsang Cho,Damon E. Turney,Gautam Ganapati Yadav,Michael Nyce,Bryan R. Wygant,Timothy N. Lambert,Sanjoy Banerjee
DOI: https://doi.org/10.3390/polym16050658
IF: 5
2024-02-29
Polymers
Abstract:Achieving commercially acceptable Zn-MnO2 rechargeable batteries depends on the reversibility of active zinc and manganese materials, and avoiding side reactions during the second electron reaction of MnO2. Typically, liquid electrolytes such as potassium hydroxide (KOH) are used for Zn-MnO2 rechargeable batteries. However, it is known that using liquid electrolytes causes the formation of electrochemically inactive materials, such as precipitation Mn3O4 or ZnMn2O4 resulting from the uncontrollable reaction of Mn3+ dissolved species with zincate ions. In this paper, hydrogel electrolytes are tested for MnO2 electrodes undergoing two-electron cycling. Improved cell safety is achieved because the hydrogel electrolyte is non-spillable, according to standards from the US Department of Transportation (DOT). The cycling of "half cells" with advanced-formulation MnO2 cathodes paired with commercial NiOOH electrodes is tested with hydrogel and a normal electrolyte, to detect changes to the zincate crossover and reaction from anode to cathode. These half cells achieved ≥700 cycles with 99% coulombic efficiency and 63% energy efficiency at C/3 rates based on the second electron capacity of MnO2. Other cycling tests with "full cells" of Zn anodes with the same MnO2 cathodes achieved ~300 cycles until reaching 50% capacity fade, a comparable performance to cells using liquid electrolyte. Electrodes dissected after cycling showed that the liquid electrolyte allowed Cu ions to migrate more than the hydrogel electrolyte. However, measurements of the Cu diffusion coefficient showed no difference between liquid and gel electrolytes; thus, it was hypothesized that the gel electrolytes reduced the occurrence of Cu short circuits by either (a) reducing electrode physical contact to the separator or (b) reducing electro-convective electrolyte transport that may be as important as diffusive transport.
polymer science
What problem does this paper attempt to address?
### Problems the Paper Aims to Solve This paper aims to address the key issues faced by zinc-manganese oxide (Zn-MnO₂) rechargeable batteries in practical applications. Specifically, the researchers hope to improve the safety and performance of the batteries by using hydrogel electrolytes and reduce the diffusion of copper ions (Cu²⁺). #### Main Issues Include: 1. **Safety Issues**: - Liquid electrolytes (such as potassium hydroxide solution) are prone to leakage, especially when the battery casing is damaged, which can lead to safety hazards during transportation and use. - Hydrogel electrolytes, due to their non-flowing nature, can significantly improve battery safety, meeting the U.S. Department of Transportation (DOT) standards for non-leakage batteries. 2. **Performance Issues**: - Liquid electrolytes can cause irreversible side reactions during charge and discharge, such as the formation of electrochemically inactive materials (like Mn₃O₄ or ZnMn₂O₄), which reduce the battery's cycle life and energy efficiency. - By using hydrogel electrolytes, researchers hope to reduce these side reactions, thereby improving the battery's cycle stability and energy efficiency. 3. **Copper Ion Diffusion Issues**: - In liquid electrolytes, copper ions (Cu²⁺) can easily migrate and deposit on the separator, leading to internal short circuits and further affecting battery performance. - By using hydrogel electrolytes, researchers hope to reduce the migration of copper ions, thereby reducing the risk of short circuits and improving battery reliability and lifespan. ### Research Methods To verify the effectiveness of hydrogel electrolytes, the researchers conducted the following experiments: - **Half-Cell Tests**: Using advanced MnO₂ cathodes paired with commercial NiOOH electrodes, they tested the performance of hydrogel electrolytes and conventional electrolytes in half-cells. - **Full-Cell Tests**: Using the same MnO₂ cathodes and zinc anodes, they tested the cycling performance of hydrogel electrolytes in full cells. - **Safety Tests**: According to DOT standards, they tested the leakage of hydrogel electrolytes when the battery casing is broken. - **Copper Ion Diffusion Tests**: They measured the diffusion coefficient of copper ions in liquid electrolytes and hydrogel electrolytes through experiments to analyze the migration behavior of copper ions. ### Results - **Safety**: Hydrogel electrolytes showed almost no leakage when the battery casing was broken, meeting DOT's non-leakage standards. - **Performance**: Half-cells and full cells using hydrogel electrolytes exhibited excellent cycling performance, achieving over 700 cycles and about 300 cycles respectively, with high coulombic efficiency and energy efficiency. - **Copper Ion Diffusion**: Hydrogel electrolytes significantly reduced the migration of copper ions, lowering the risk of short circuits. ### Conclusion By using hydrogel electrolytes, the researchers successfully improved the safety and performance of Zn-MnO₂ rechargeable batteries and reduced the diffusion of copper ions, providing a new approach for developing high-performance, high-safety zinc-manganese oxide batteries.