Abstract:Ammonia gas can be simultaneously used as a reductant and nitrogen source to prepare TiN from titania. In this work, the mechanisms on reduction and nitridation of micron–sized anatase with ammonia gas have been investigated, using both thermodynamic and experimental studies. The thermodynamic analysis indicated that reduction and nitridation of TiO2 by NH3 was feasible. Anatase will undergo different paths to form TiN, depending on the reaction temperature. Upon heating, NH3 was seen to partially decompose into N2 and H2, although the actual NH3 decomposition ratio was less than the theoretical value. The experimental results indicated that the obtained titanium nitride was non–stoichiometric (TiNxO1‐x, x≤1), as it contained a certain amount of oxygen. Based on the phase transformation and X–ray photoelectron spectroscopy analysis, the reduction and nitridation routes were deduced: TiO2 reacted with NH3 to form TiNxO1‐x directly, at lower temperatures, and followed the path TiO2→TinO2n–1→TiNxO1‐x, at higher temperatures. TinO2n–1 was determined to be Ti4O7 and Ti3O5 at 1100 °C and 1200 °C, respectively. Reaction temperature and time significantly affected the oxygen and nitrogen contents in TiNxO1‐x, with the lattice parameter of roasted products gradually increasing—approaching those of pure TiN—with an increase in reaction temperature and holding time. At the same time, the content of oxygen in TiNxO1‐x decreased, and its nitrogen content correspondingly increased.

Titanium Nitride Synthesis during Double Mechanical Activation of Titanium—in Argon and in Nitrogen

Use of Nitrogen Gas in High-Speed Milling of Ti-6Al-4V

Supercritical Combustion Synthesis of Titanium Nitride

Anisotropic Phase Transformation Mechanism on Coarse-Grained and Fine-Grained Pure Titanium at Low-Temperature Plasma Nitriding

Waste Conversion into High-Value Ceramics: Carbothermal Nitridation Synthesis of Titanium Nitride Nanoparticles Using Automotive Shredder Waste.

Synthesis of titanium nitride via hybrid nanocomposites based on mesoporous TiO2/acrylonitrile

Plasma Nitridation and Mechanical Properties of Pure Titanium Casts

Synthesis of Nanopowders of Titanium Nitride by In-Situ Nitridation of Titanium Oxide

Mechanochemically assisted synthesis of titanium carbonitride from metal and organic precursor

Photocatalytic Activity of Nitrogen Doped Nano-titanias and Titanium Nitride towards Methylene Blue Decolouration

Mechanosynthesis Mechanism of Tic Powders

Reactive nitrogen plasma spray coating of titanium nitride: plasma torch design and coating analysis

Metal Reduction of Nitrides in a Self-Propagating Way

Titanium Nitride (TiN) Germination and Growth during Vacuum Arc Remelting of a Maraging Steel

Plasma Spray Deposition Enhancement of Titanium Nitride Layer Using Nitrogen-Contained Plasma Irradiation of Titanium Substrate as a Pre-spraying Method

Mechanism on reduction and nitridation of micrometer‐sized titania with ammonia gas

Effect of Mechanical Activation of Al-Ti-B Powder Mixture on Phase Composition and Structure of Al-TiB2 Composite Materials Obtained by Self-Propagating High-Temperature Synthesis (SHS)

Synthesis of Uniform Titanium Nitride Nanocrystalline Powders Via a Reduction–Hydrogenation–Dehydrogenation–Nitridation Route

Combustion Synthesis of Ti(C,N) Powder

Thermochemical Processes Occurring in a Titanium Nitride Coating under the Effect of Thermal Laser Pulses

Double-Glow Plasma Surface Alloying of BTi-62421S Alloys: Regulation of Microstructure Properties