Abstract:The ammonia synthesis activities of the anti-perovskite nitrides Co3CuN and Ni3CuN have been compared to investigate the possible metal composition-activity relationship. Post-reaction elemental analysis showed that the activity for both nitrides was due to loss of lattice nitrogen rather than a catalytic process. Co3CuN was observed to convert a higher percentage of lattice nitrogen to ammonia than Ni3CuN and was active at a lower temperature. The loss of lattice nitrogen was revealed to be topotactic and Co3Cu and Ni3Cu were formed during the reaction. Therefore, the anti-perovskite nitrides may be of interest as reagents for the formation of ammonia through chemical looping. The regeneration of the nitrides was achieved by ammonolysis of the corresponding metal alloys. However, regeneration using N2 was shown to be challenging. In order to understand the difference in reactivity between the two nitrides, DFT techniques were applied to investigate the thermodynamics of the processes involved in the evolution of lattice nitrogen to the gas phase via conversion to N2 or NH3, revealing key differences in the energetics of bulk conversion of the anti-perovskite to the alloy phase, and in loss of surface N from the stable low-index N-terminated (111) and (100) facets. Computational modelling of the density of states (DOS) at the Fermi level was performed. It was shown that the Ni and Co d states contributed to the density of states and that the Cu d states only contributed to the DOS for Co3CuN. The anti-perovskite Co3MoN has been investigated as comparisons with Co3Mo3N may give an insight into the role structure type plays in the ammonia synthesis activity. The XRD pattern and elemental analysis for the synthesised material revealed that an amorphous phase was present that contained nitrogen. In contrast to Co3CuN and Ni3CuN, the material was shown to have steady state activity at 400 °C with a rate of 92 ± 15 μmol h-1 g-1. Therefore, it appears that metal composition has an influence on the stability and activity of the anti-perovskite nitrides.

A Comparison of the Mechanisms and Activation Barriers for Ammonia Synthesis on Metal Nitrides (Ta3N5, Mn6N5, Fe3Mo3N, Co3Mo3N)

Preparation and Surface Chemistry Study of Supported Cobalt Molybdenum Metal Nitrides

Experimental and theoretical investigations on the anti-perovskite nitrides Co3CuN, Ni3CuN and Co3MoN for ammonia synthesis

Synthesis and Structural Study of Substituted Ternary Nitrides for Ammonia Production

Manipulating the Geometric and Electronic Structures of Manganese Nitrides for Ammonia Synthesis

Enhancing Ammonia Synthesis on Co3Mo3N via Metal Support Interactions on a Single‐crystalline MgO Support

Unique Catalytic Mechanism for Ru-Loaded Ternary Intermetallic Electrides for Ammonia Synthesis

Ammonia Synthesis on Ternary LaSi‐based Electrides: Tuning the Catalytic Mechanism by the Third Metal

Dissociative and Associative Concerted Mechanism for Ammonia Synthesis over Co-Based Catalyst

Computational evaluation of FeMo heteroatom coeffect induced high electroreduction activity of N2-to-NH3

Engaging the Concepts of Bimetallicity and Mechanical Strain for N2 Activation: A Computational Exploration

Alkali and Alkaline Earth Hydrides-Driven N2 Activation and Transformation over Mn Nitride Catalyst.

Insight into the Dynamic Evolution of Co3Mo3N Bimetallic Nitride Surface During Ammonia Synthesis

Catalytic Ammonia Synthesis over Mo Nitride/ZSM‐5

Design Principle of Molybdenum-Based Metal Nitrides for Lattice Nitrogen-Mediated Ammonia Production

Highly active manganese nitride-europium nitride catalyst for ammonia synthesis

Tailoring of Three-Atom Metal Cluster Catalysts for Ammonia Synthesis

Insight into the Dynamic Evolution of Co 3 Mo 3 N Bimetallic Nitride Surface during Ammonia Synthesis

The synthesis mechanism of nitrogen to ammonia on the Fe, Co, Ni-doped Cu(1 0 0) Surface: A DFT study

Exploring trimetallic clusters containing alkali and alkaline earth metal atoms with high activity for nitrogen activation

Catalytic ammonia synthesis by supported molybdenum nitride: insight into the support effect