Abstract:The ammonia synthesis activities of the anti-perovskite nitrides Co3CuN and Ni3CuN have been compared to investigate the possible metal composition-activity relationship. Post-reaction elemental analysis showed that the activity for both nitrides was due to loss of lattice nitrogen rather than a catalytic process. Co3CuN was observed to convert a higher percentage of lattice nitrogen to ammonia than Ni3CuN and was active at a lower temperature. The loss of lattice nitrogen was revealed to be topotactic and Co3Cu and Ni3Cu were formed during the reaction. Therefore, the anti-perovskite nitrides may be of interest as reagents for the formation of ammonia through chemical looping. The regeneration of the nitrides was achieved by ammonolysis of the corresponding metal alloys. However, regeneration using N2 was shown to be challenging. In order to understand the difference in reactivity between the two nitrides, DFT techniques were applied to investigate the thermodynamics of the processes involved in the evolution of lattice nitrogen to the gas phase via conversion to N2 or NH3, revealing key differences in the energetics of bulk conversion of the anti-perovskite to the alloy phase, and in loss of surface N from the stable low-index N-terminated (111) and (100) facets. Computational modelling of the density of states (DOS) at the Fermi level was performed. It was shown that the Ni and Co d states contributed to the density of states and that the Cu d states only contributed to the DOS for Co3CuN. The anti-perovskite Co3MoN has been investigated as comparisons with Co3Mo3N may give an insight into the role structure type plays in the ammonia synthesis activity. The XRD pattern and elemental analysis for the synthesised material revealed that an amorphous phase was present that contained nitrogen. In contrast to Co3CuN and Ni3CuN, the material was shown to have steady state activity at 400 °C with a rate of 92 ± 15 μmol h-1 g-1. Therefore, it appears that metal composition has an influence on the stability and activity of the anti-perovskite nitrides.

Design Principle of Molybdenum-Based Metal Nitrides for Lattice Nitrogen-Mediated Ammonia Production

Rational Design Synergistic Metal-Free Dual-Atom Electrocatalyst for N2 to NH3 Reaction on G-Cn: A First Principle Study

Transition metal enhanced chromium nitride as composite nitrogen carrier for sustainable chemical looping ammonia synthesis

Manipulating the Geometric and Electronic Structures of Manganese Nitrides for Ammonia Synthesis

Synthesis and Structural Study of Substituted Ternary Nitrides for Ammonia Production

Key Role of Local Chemistry in Lattice Nitrogen‐Participated N2‐to‐NH3 Electrocatalytic Cycle over Nitrides

Graphdiyne/main-group metal elements sandwich structure as a promising single atom electrocatalyst for nitrogen reduction: A theoretical investigation

Mo-Doped Metal–Organic Frameworks for Efficient Nitrogen Reduction Reaction: A Density Functional Theory Study

A Metal-Sulfur-Carbon Catalyst Mimicking the Two-Component Architecture of Nitrogenase

Thermodynamic and kinetic considerations of nitrogen carriers for chemical looping ammonia synthesis

Tackling the Activity Trend of Metal‐Loaded Metal Nitride Catalysts for NH3 Synthesis by a First‐Principles Microkinetic Study

Tailoring of Three-Atom Metal Cluster Catalysts for Ammonia Synthesis

Design principles for transition metal nitride stability and ammonia generation in acid

Trimetallic Single-Cluster Catalysts for Electrochemical Nitrogen Reduction Reaction: Activity Prediction, Mechanism, and Electronic Descriptor

Insight into the Dynamic Evolution of Co3Mo3N Bimetallic Nitride Surface During Ammonia Synthesis

Crystal structures of molybdenum borides dictate electrocatalytic ammonia synthesis efficiency

Alkali and Alkaline Earth Hydrides-Driven N2 Activation and Transformation over Mn Nitride Catalyst.

A New Molybdenum Nitride Catalyst with Rhombohedral MoS2 Structure for Hydrogenation Applications.

Experimental and theoretical investigations on the anti-perovskite nitrides Co3CuN, Ni3CuN and Co3MoN for ammonia synthesis

Valence Engineering at the Interface of MoS2/Mo2C Heterostructure for Bionic Nitrogen Reduction

Spatial confinement and electron transfer moderating Mo N bond strength for superior ammonia decomposition catalysis