Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Particulate matter capturing over manganese dioxides with different crystal structures

Mechanistic investigation on the Hg 0 elimination ability of MnO x –CeO x nanorod adsorbents: effects of Mn/Ce molar ratio

Constructing Carbon-Coated Fe3O4 Hierarchical Microstructures with a Porous Structure and Their Excellent Cr(VI) Ion Removal Properties

Synthesis, Characterization, and Kinetic Study of Mn(DPM)3 Used As Precursor for MOCVD

Controlled Morphology of One-Dimensional Manganese Dioxide with Dramatic Enhancing Removal Efficiency to Heavy Metal Ions in Aqueous Solution

Tuning the crystallinity of MnO2 oxidant to achieve highly efficient pollutant degradation

Efficient removal of Pb(II) ions using manganese oxides: the role of crystal structure

An Advanced Dual‐Function MnO 2 ‐Fabric Air Filter Combining Catalytic Oxidation of Formaldehyde and High‐Efficiency Fine Particulate Matter Removal

Catalytic Decomposition of Gaseous Ozone over Manganese Dioxides with Different Crystal Structures

Adsorption of PO 4 3- , Cd(II), Pb(II), Cu(II), As(III), and As(V) using a carbonised Mn-based metal–organic framework

Morphological impact of 1-dimensional → 3-dimensional manganese dioxides on ozone catalytic decomposition correlated with crystal facet and lattice oxygen mobility

Phase-activity relationship of MnO2 nanomaterials in periodate oxidation for organic pollutant degradation

MnO 2 -loaded flexible mullite nanofiber filter materials for removing particulate matter and formaldehyde from indoor air

Comparing Mn-based oxides filters started by KMnO4 versus K2FeO4 for ammonium and manganese removal: Formation mechanism of active species

Effects of Mno2 Crystal Structure and Surface Property on the Nh3-Scr Reaction at Low Temperature

The effect of crystal structure of MnO2 electrode on DMAC removal: degradation performance, mechanism, and application evaluation

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Manganese Oxyhydroxide And Oxide Nanofibers For High Efficiency Degradation Of Organic Pollutants

Efficient removal of aqueous organic pollutants by well-ordered layered manganese oxide nanocomposites: Impacts of interlayer spacing and nanoconfinement

Preparation and Characterization of Hierarchically Porous SiO2@C@MnO2 Monoliths

Crystal facet engineering of K-OMS-2 for active site identification in catalytic ozone decomposition