Efficient removal of aqueous organic pollutants by well-ordered layered manganese oxide nanocomposites: Impacts of interlayer spacing and nanoconfinement

Zhiqiang Wang,Yafang Shi,Kangjie Yang,Huiqiang Yang,Haoran Zhao,Mengning Xi,Chi Zhang,Lingyan Zhu,Hanzhong Jia

DOI: https://doi.org/10.1016/j.cej.2023.144830

IF: 15.1

2023-07-21

Chemical Engineering Journal

Abstract:Although manganese oxide is able to spontaneously oxidize organic contaminants in nature, the slow kinetics limit its application in engineered water treatment processes. Herein, we prepared well-ordered layered manganese oxides (LMOs) with adjustable interlayer distances using cetyltrimethylammonium bromine as a guest molecule, which were applied to degrade 3-chlorophenol as an example of organic pollutants. The ordering of the layered structure was found to be highly dependent on the molar ratio of cetyltrimethylammonium ion (CTA + ) to Mn in the solutions (range 0–1.2). The maximum interlayer spacing (11.27 Å) was obtained at a molar ratio was 1.0 (LMO-1.0), which reduces the steric hindrance for 3-chlorophenol entering the interlayers. Additionally, the surface of the LMOs becomes more hydrophobic as their molar ratio increased, further favors adsorption of 3-chlorophenol on the LMO-1.0. The LMO-1.0 provides a constrained reaction environment, which increases the probability of 3-chlorophenol interacting with the active species as well as promotes the production and enrichment of superoxide radical (O 2 •− ). Consequently, the degradation rate constant of 3-chlorophenol (0.446 min −1 ) is two orders of magnitude higher compared to the unconfined bulk phase (0.004 min −1 ). These findings provide useful insights into the development of Mn-based layered materials for water purification.

engineering, chemical, environmental