Roles of reinforcements in twin nucleation and nano-α precipitation in the hybrid TiB/TiC-reinforced titanium matrix composites during high-temperature fatigue

Xiaoyan Wang,Shaopeng Li,Yuanfei Han,Guangfa Huang,Jianwei Mao,Weijie Lu

DOI: https://doi.org/10.1016/j.scriptamat.2021.113758

IF: 6.302

2021-04-01

Scripta Materialia

Abstract:<p>Almost no studies have been carried out on the roles of reinforcements in the microstructural evolution of the titanium matrix composites (TMCs) during high-temperature fatigue. In this paper, short TiB fibers and TiC particles enhanced the dislocation accumulation in the primary α and β phases, and we found a new phenomenon in which <span class="math"><math>{101¯2}</math></span> deformation twins nucleated at two interfaces: the α/β interface and the reinforcement/matrix interface. Dislocations can decompose into twinning dislocations due to the local stress concentration and result in twin nucleation. Moreover, under thermal activation, dislocations act as channels for rapid diffusion of elements (V, Al and O), resulting in numerous nano-α phases precipitating in the β phase, increasing the local stress concentration at primary α/β interface, which was conducive to twin nucleation. Our work helps further clarify the roles of reinforcements and to supplement the mechanism underlying TMC fracture during high-temperature fatigue.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the role of reinforcements (such as TiB fibers and TiC particles) in the microstructural evolution of Titanium Matrix Composites (TMCs) under high - temperature fatigue conditions, especially their influence on twin nucleation and nano - α precipitation. Although previous studies have explored the fatigue behavior of titanium alloys at high temperatures, there are relatively few studies on the specific role of reinforcements in the microstructural evolution of TMCs, especially under high - temperature fatigue conditions. Therefore, through experiments and analysis, this paper aims to reveal how these reinforcements affect the microstructural changes of TMCs during high - temperature fatigue, thereby further understanding the fracture mechanism of TMCs under high - temperature fatigue conditions.

Specifically, the paper focuses on the following points:
1. **Role of reinforcements**: Explore how short TiB fibers and TiC particles enhance dislocation accumulation, leading to the nucleation of {1012} deformation twins at the α/β interface and the reinforcement/matrix interface.
2. **Nano - α precipitation**: Study how, under thermal activation, dislocations act as fast diffusion channels, causing rapid diffusion of V, Al, and O elements in the β phase and the formation of a large number of nano - α phases.
3. **Crack propagation path**: Analyze the influence of reinforcements on the crack propagation path, especially how twin nucleation affects crack propagation.
4. **Microstructural evolution mechanism**: Reveal the contribution of reinforcements to microstructural evolution during high - temperature fatigue, including phase transformation and twin nucleation, and how these changes affect the fatigue properties of the material.

Through these studies, the paper aims to supplement and improve the fracture mechanism of TMCs under high - temperature fatigue conditions and provide new ideas for improving the high - temperature fatigue performance of TMCs.