The Role of High-Index Twinning on Hierarchical Α Microstructure in a Metastable Β Ti-5Al-5Mo-5V-3Cr Alloy

Li Dian,Zhang Xing,Zhao Wenrui,Merrill H. Darlene,Meyer Noah T.,Antonov Stoichko,Liao Yiliang,Zheng Yufeng
DOI: https://doi.org/10.1007/s11837-021-04757-0
2021-01-01
JOM
Abstract:Hierarchical α microstructure in a metastable β Ti-5Al-5Mo-5V-3Cr (wt%, Ti-5553) alloy has been investigated using scanning electron microscopy and transmission electron microscopy. Novel high-index {10 9 3}<3 3 1>β type deformation twins were characterized in the 10% cold-rolled Ti-5553. Without the pre-formed deformation twins, refined α microstructure and super-refined α microstructure were achieved in Ti-5553 using rapid up-quenching and slow heating treatment, respectively. On the contrary, with the pre-formed {10 9 3}<3 3 1> β deformation twins in the β matrix, hierarchical α microstructure was generated in Ti-5553, whether rapid up-quenching or slow heating treatment was adopted. It is observed that a layer of α phase precipitates from pre-formed {10 9 3}<3 3 1>β twin boundary and grows along the twin boundary. α sub-layers and fine-scale α precipitates form in the interior of pre-formed {10 9 3}<3 3 1>β twin. It is speculated that the large number of dislocations, metastable ω particles and α″ phase present as the substructure in the {10 9 3}<3 3 1>β twin may act as favorable nucleation sites for α sub-layers and fine-scale α precipitates. Thus, our work indicates that high-index {10 9 3}<3 3 1>β twin may assist the formation of hierarchical α microstructure in the metastable β Ti-5553 alloy.
What problem does this paper attempt to address?