Abstract:A simple sacrificial template method was used to prepare Co/C composite with cobalt nanoparticles embedded in nitrogen-doped polyporous graphite carbon as an efficient electromagnetic wave (EMW) absorbent. Effects of solvent polarity, ratio of Co<sup>2+</sup> to 2-methylimidazole and pH value of reaction system on precursor metal–organic skeleton ZIF-67 were systematically studied by a single variable method, and then the optimal preparation process was obtained. Thermal decomposition time and temperature of precursor ZIF-67 are the keys to the formations of ferromagnetic metal cobalt particles and carbon matrix. Therefore, effects of calcined temperature in inert atmosphere on the carbon content, graphitization degree, magnetic properties and microwave-absorbing performances of Co/C composite prepared were studied, and then nitrogen-doped porous composite Co/C composed of a highly dispersed core–shell Co@graphite nanoparticles coated by amorphous carbon skeleton was successfully prepared by optimizing pyrolysis technology. Composite Co/C-900 obtained by ZIF-67 calcinated at 900 °C exhibits excellent EMW absorption performances at low filling amount; its maximum reflective loss (RL<sub>max</sub>) reaches − 34.41 dB at 17.49 GHz with the test thickness of 2.0 mm only, and most importantly, when the test thickness is 2.5 mm, its effective absorption bandwidth (RL < − 10 dB) reaches 7.37 GHz (10.18–17.5 GHz), spanning the X and Ku bands. The synergistic effects of the self-loss (dielectric loss and magnetic dissipation) and structural attenuation (multiple scattering and interface polarization) of Co/C-900 obtained greatly improve its impedance matching with free space and attenuation coefficients to EMW, significantly widening its effective bandwidth. As a new high-performance EMW absorbent with thin thickness, light weight, strong absorption capacity and wide bandwidth, the Co/C composite optimized by precursor preparation and calcination process should have a broad application prospect.

Facile synthesis of Co/SC microwave absorbents by recycling coal hydrogasification residue

Achievement of excellent microwave absorption on the Co/C-based composite from coal hydrogasification residue

Facile Fabrication of Co-doped Porous Carbon from Coal Hydrogasification Semi-Coke for Efficient Microwave Absorption

Facile synthesis of Co-loaded ceramic composite absorbents via gangue recycling

Facile fabrication of sheet-like cobalt/carbon composites for microwave absorption

Co3O4 Nanoparticle-Modified Porous Carbons with High Microwave Absorption Performances

Fabrication of flexible waterborne polyurethane/Fe-doped residual carbon from coal hydrogasification semi-coke composites for high-performance microwave absorption

Co/CoO/Lotus Seedpod Nanoporous Carbon Composites Reduced from Co 3 O 4 for High-Performance Microwave Absorbers

Environmentally friendly bark-derived Co-Doped porous carbon composites for microwave absorption

Hierarchical Porous Carbon/Co Nanocomposites Derived from Biomass for High-Performance Microwave Absorption

Preparation and properties of cobalt oxides coated carbon fibers as microwave-absorbing materials

Facile synthesis of cobalt nanoparticles embedded in a rod-like porous carbon matrix with excellent electromagnetic wave absorption performance

Sterculia lychnophora seed-derived porous carbon@CoFe2O4 composites with efficient microwave absorption performance

Preparation of Co/C Composites Derived from Zn/Co-ZIFs and Their Microwave Absorption Properties

Coal gasification fine slag residual carbon decorated with hollow-spherical Fe3O4 nanoparticles for microwave absorption

Lightweight, Low-Cost Co2SiO4@diatomite Core-Shell Composite Material for High-Efficiency Microwave Absorption

A hierarchical Co @ mesoporous C/ macroporous C sheet composite derived from bimetallic MOF and oroxylum indicum for enhanced microwave absorption

Co/C broad band electromagnetic wave absorption composite derived from preferred precursor ZIF-67: preparation and performance

Solvothermal assisted synthesis of CoFe2O4/CNTs nanocomposite and their enhanced microwave absorbing properties

Fabrication and Microwave Absorption Properties of Core-Shell Structure Nanocomposite Based on Modified Anthracite Coal

One-pot synthesis of coal gangue–derived NiCG composite for enhancing microwave absorption