Enhanced electromagnetic wave absorption of hybrid-architectures Co@ SiOxC
Jianwen Ge,Yu Cui,Li Liu,Rui Li,Fandi Meng,Fuhui Wang
DOI: https://doi.org/10.1016/j.jallcom.2020.154442
IF: 6.2
2020-08-01
Journal of Alloys and Compounds
Abstract:<p>Rational design on the well wrapped core-shell microstructure of SiO<sub>x</sub>C composites was successfully conducted through reduction process of cobalt, efficient condensation reaction of KH-550 silane coupling agent as well as high temperature calcination. The SiO<sub>x</sub>C shell possessed 3D cross-linked network structure consisting of dielectric carbon and silicon composition for optimal electromagnetic matching. The microstructure, morphology, elements distribution, electromagnetic property and microwave absorption performance were fully characterized, respectively. This SiO<sub>x</sub>C shell effectively inhibited the agglomeration of cobalt particles, and regulated the complex electromagnetic parameters by decreasing permittivity and introducing polarization relaxation, all of which determined the efficient reflection loss with RL<sub>min</sub> value of −60.3 dB at 16.2 GHz and matching thickness of only 2.05 mm. Meanwhile, the effective absorption band is up to 7.1 GHz at 2.3 mm. By optimizing of core-shell structure and material components, the high-absorption performance was obtained through impedance matching, multi-interfacial polarizations, dipole (or defects) polarization and magnetic loss. Therefore, the SiO<sub>x</sub>C composites present a facile and promising route toward the design of large-scale-preparation and excellent microwave absorbing materials.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering