Electrospun PVA Nanofibrous Membranes Reinforced with Silver Nanoparticles Impregnated Cellulosic Fibers: Morphology and Antibacterial Property

Jie Yan,Dong Wang,Tian Bai,Wanli Cheng,Guangping Han,Xiaohui Ni,Q. Sheldon Shi

DOI: https://doi.org/10.1007/s40242-021-1089-3

IF: 3.1

2021-04-08

Chemical Research in Chinese Universities

Abstract:<span><b>T</b>o enhance the mechanical and antibacterial properties of silver nanoparticle impregnated cellulosic fibers, carboxy-cellulose nanocrystals(CCNs) were grafted with chitooligosaccharide(COS), which was used as a stabilizer for silver nanoparticles (AgNPs). Nanofibrous membranes reinforced with silver nanoparticle impregnated cellulosic fibers(CCN-COS-AgNP) were prepared <i>via</i> electrospinning using polyvinyl alcohol(PVA) as a matrix. The effects of CCN-COS-AgNP contents on the morphology, surface composition, mechanical properties, and antibacterial performances of the prepared CCN-COS-AgNP/PVA membranes were examined. The addition of CCN-COS-AgNP certainly improved the mechanical properties and antibacterial performances of the PVA nanofibers. The tensile strength was significantly increased from 4.40 MPa to 8.60 MPa when 8% CCN-COS-AgNP(mass ratio) was introduced. When 10%(mass ratio) CCN-COS-AgNP was added, the nanofibers showed an excellent antibacterial activity for <i>S. aureus</i>(<i>Staphylococcus aureus</i>) and <i>E. coli</i>(<i>Escherichia coli</i>), with the maximum inhibition zones of 2.30 and 1.60 cm, respectively. Moreover, the 2%(mass ratio) CCN-COS-AgNP/PVA fibrous membrane showed 126% cell viability for mg63 human osteoblasts. The electrospun PVA membrane has great potential application in biomedical field.</span>

chemistry, multidisciplinary

What problem does this paper attempt to address?

The paper aims to address the following issues:

1. **Enhancing Mechanical Properties**: By introducing carboxylated cellulose nanocrystals (CCN)-chitosan oligosaccharide (COS)-silver nanoparticles (AgNP) composites into polyvinyl alcohol (PVA) nanofiber membranes to enhance their mechanical properties.

2. **Improving Antibacterial Properties**: By incorporating CCN-COS-AgNP composites into PVA nanofiber membranes to improve their antibacterial properties against Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli).

3. **Optimizing Biocompatibility**: Investigating the effects of different contents of CCN-COS-AgNP on the cytotoxicity of PVA nanofiber membranes to ensure their safety in biomedical applications.

Specifically, the paper prepared CCN-COS-AgNP/PVA nanofiber membranes through chemical modification and electrospinning techniques and systematically studied the effects of different contents of CCN-COS-AgNP on the microstructure, surface composition, mechanical properties, and antibacterial properties of the fiber membranes. The experimental results showed that when the mass ratio of CCN-COS-AgNP was 8%, the tensile strength of the fiber membrane significantly increased to 8.60 MPa; when the mass ratio was 10%, the inhibition zone diameters against S. aureus and E. coli reached 2.30 cm and 1.60 cm, respectively. Additionally, when the mass ratio of CCN-COS-AgNP was 2%, the cell viability of human osteoblasts (mg63) on the fiber membrane reached 126%. These results indicate that CCN-COS-AgNP/PVA nanofiber membranes exhibit excellent mechanical and antibacterial properties and show good biocompatibility at low contents, suggesting potential biomedical applications.