Additive manufacturing of VCoNi medium-entropy alloy: microstructure evolution and mechanical properties

Abdukadir Amar,Mingliang Wang,Lingkun Zhang,Jinfeng Li,Liufei Huang,Hongwei Yan,Yongan Zhang,Yiping Lu

DOI: https://doi.org/10.1016/j.addma.2023.103522

IF: 11

2023-03-25

Additive Manufacturing

Abstract:As a novel class of promising materials, high- and medium- entropy alloys (HEAs and MEAs) have attracted extensive attention due to their outstanding properties beyond those of conventional alloys. The conventional fabrication process of HEAs and MEAs suffers from significant limitations due to the intrinsic requirements. On the other hand, additive manufacturing (AM) has provided a new approach to producing large-scale and complex-shaped metallic parts. This study examined the microstructure evolution and mechanical properties of VCoNi MEA sample fabricated by laser melting deposition (LMD). The repeated cellular-columnar-equiaxed heterogeneous microstructure was found to occupy the whole cross-sectional area of single-wall sample, which was related to the degree of constitutional undercooling evolution and the repeated layer-by-layer deposition nature of the LMD process. The mechanical properties of samples varied from top to bottom, mainly due to the σ phase content variation in the different location. At the bottom of sample, tensile elongation and ultimate tensile strength were no less than 10% and 1.5 GPa, respectively, while at the top, these parameters were 19.5% and ≥ 1.2 GPa. The above strength-ductility combination was comparable to the best AM-forming eutectic high entropy alloys (EHEAs), but superior than most reported AM alloys, which strongly indicates its great potential in structural applications.

engineering, manufacturing,materials science, multidisciplinary