Structural and electrical studies of Nd and Gd co-doped zirconia electrolytes for IT-SOFC applications

B. Swamy,Kasarapu Venkataramana,Chittimadula Madhuri,Ashok Bhogi,C. Vishnuvardhan Reddy

DOI: https://doi.org/10.1007/s11581-024-05448-x

IF: 2.961

2024-02-23

Ionics

Abstract:The Nd and Gd co-doped zirconia Zr 1–x–y Nd x Gd y O 2–δ ( x , y = 0.025, 0.05, 0.075, and 0.10) system of materials were prepared through a modified sol–gel route. Sintering of the samples was conducted using conventional sintering at 1300 °C for 6 h. The prepared materials are characterized by powder X-ray diffraction (P–XRD), scanning electron microscopy with energy dispersive spectroscope (SEM with EDS), Fourier transform infrared (FTIR), Raman, and impedance spectroscopy. The dense electrolyte pellets are produced with co-doping in zirconia. P–XRD confirmed the formation of samples with single phases with stabilized cubic structure even after the sintering of co-doped zirconia samples. SEM and EDS revealed good density in surface microstructure and elemental confirmation in all the compositions. XRD and SEM studies also revealed the highest relative density and small grain size of Zr 0.85 Nd 0.075 Gd 0.075 O 2–δ . FTIR disclosed the absorption bands corresponding to the chemical bonds of oxides in the compositions, and the findings are consistent with the P–XRD data. Raman spectroscopy analysis revealed the further phase confirmation of cubic structure. Impedance spectroscopy unveiled the enhanced electrical properties, i.e., enhanced ionic conductivity and small activation energy of NGZ7.5. The enhanced ionic conductivity, i.e., 0.47 × 10 −2 S/cm at 550 °C with the stabilized cubic structure of Zr 0.85 Nd 0.075 Gd 0.075 O 2–δ sample makes it suitable for solid electrolytes towards intermediate temperature solid oxide fuel cell applications.

chemistry, physical,physics, condensed matter,electrochemistry