Abstract:In response to the demands for high frequency, miniaturization, and high integration in electronic devices, such as inductors and DC-DC convertors, nickel–zinc ferrite thin films exhibit significant application value and development potential. For regulating the magnetic properties and microstructure of spin-sprayed polycrystalline ferrite materials, a comprehensive understanding of the impact of oxidant concentration on film reaction is essential. This study finds that as the concentration of the NaNO2 oxidant increases, the grain size of the nickel–zinc ferrite thin film samples progressively enlarges. Due to the preferential occupation of iron ions at the B sites, the saturation magnetization correspondingly increases. However, when the oxidant concentration becomes excessive, the preferential (222) orientation growth of the film is disrupted, leading to the agglomeration and uneven growth of grains, transitioning from triangular plate-like to spherical in shape. This increase in grain size alters the magnetization mechanism of the thin film, predominantly favoring domain wall movement. Upon analyzing the microstructure and magnetic characteristics, it becomes evident that the concentration of oxidant is a key determinant in the spin-spray deposition process.
What problem does this paper attempt to address?
This paper attempts to address the impact of oxidant concentration on the reaction kinetics, microstructure, and magnetic properties of nickel-zinc ferrite films prepared by spin-spray deposition. Specifically, the study aims to explore how different concentrations of the oxidant (NaNO2) affect key characteristics such as grain size, magnetic saturation, and magnetic anisotropy of the films.
### Main Research Questions:
1. **Effect of oxidant concentration on grain growth**: How does the grain size of the film change with increasing oxidant concentration?
2. **Effect of oxidant concentration on magnetic properties**: How does the oxidant concentration affect the magnetic saturation and coercivity of the film?
3. **Effect of oxidant concentration on the microstructure of the film**: How does the oxidant concentration influence the crystal orientation and grain morphology of the film?
4. **Effect of oxidant concentration on electromagnetic properties**: How does the oxidant concentration affect the magnetic permeability and cutoff frequency of the film?
### Research Background:
In modern electronic systems, there is a growing demand for high frequency, miniaturization, and high integration. Nickel-zinc ferrite films, with their high resistivity and low high-frequency eddy current loss, have become ideal materials to replace traditional metallic magnetic films. However, traditional deposition methods such as sputtering and vacuum evaporation require high-temperature annealing, which is incompatible with semiconductor processes. Therefore, developing low-temperature deposition techniques, such as spin-spray deposition, is particularly important. Spin-spray deposition can achieve the crystallization of soft magnetic ferrite films at lower temperatures (≤130°C), thus meeting the requirements of semiconductor processes.
### Research Methods:
- **Experimental Design**: A series of NaNO2 solutions with different concentrations (1, 2, 3, 4, 5 mmol/L) were prepared, and Ni0.34Zn0.16Fe2.50O4 films were deposited on glass substrates using the spin-spray deposition method.
- **Characterization Techniques**: The structure, micro-morphology, magnetic properties, and electromagnetic properties of the films were characterized using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), vibrating sample magnetometer (VSM), thermal imager, network analyzer, and atomic force microscope (AFM).
### Research Results:
- **Grain Size**: With the increase in oxidant concentration, the grain size of the film gradually increased, but when the concentration exceeded 3 mmol/L, the grains began to aggregate and grow unevenly.
- **Magnetic Properties**: The increase in oxidant concentration led to iron ions preferentially occupying B sites, thereby increasing magnetic saturation. However, when the concentration exceeded 3 mmol/L, the preferred orientation growth of the (222) plane was disrupted, and the magnetic saturation decreased.
- **Microstructure**: The increase in oxidant concentration changed the grains of the film from triangular plate-like to spherical, and the increase in grain size altered the magnetization mechanism of the film, mainly manifested as domain wall motion.
- **Electromagnetic Properties**: The increase in oxidant concentration first increased and then decreased the magnetic permeability of the film, with the maximum value appearing at 3 mmol/L.
### Conclusion:
Oxidant concentration is a key factor affecting the reaction kinetics, microstructure, and magnetic properties of films during the spin-spray deposition process. By precisely controlling the oxidant concentration, the magnetic and electromagnetic properties of the films can be optimized to meet the demands of high-frequency electronic applications.