Abstract:With the increasing demand for the high agility and fast response of high-level equipment in the aerospace and energy power fields, it is increasingly urgent to improve the performance of the high-temperature and wear resistance of the corresponding high-level components. Ceramic-reinforced titanium matrix composites have excellent high-temperature and wear resistance, but, in laser additive manufacturing, the primary ceramic phase is coarse, and the morphology of the ceramic phase is difficult to control, which limits their further development. In this investigation, a follow-up ultrasonic-assisted laser-additive-manufacturing method was proposed to prepare a 30 wt.% TiC/Ti6Al4V composite coating on a Ti6Al4V surface. Under the effects of ultrasonic cavitation and acoustic streaming, the content of the unmelted TiC was reduced, the dendritic primary TiC in the solidification process was broken and the distribution uniformity of the primary TiC was improved. The content of the unmelted TiC in the composite coating decreased significantly under ultrasonic action, and it was only 50.23% of that without ultrasonic action. At the same time, the average size of the dendritic primary TiC in the composite coating decreased from 61.59 μm to 27.04 μm, which was 56.10% smaller than that without ultrasonic action. The average microhardness of the composite coating reached the maximum of 656.70 HV0.2 under ultrasonic power, and it was 83.21% higher than that of the Ti6Al4V substrate, and 26.44% higher than that of the composite coating without ultrasonic power. Due to the ultrasonic-cavitation and acoustic-streaming effects, the content of the unmelted TiC obviously decreased, so that the average friction coefficient of the composite coating increased, and the wear mechanism changed from abrasive wear to adhesive wear.

Wetting tuning of Al/B 4 C interface via femtosecond laser irradiation

Improving Al Wettability on B 4 C by Transition Metal Doping: a Combined DFT and Experiment Study

Laser ablative patterning of B4C and MoAlB ceramics for hydrophobic surfaces

Simultaneously Increasing the Mechanical Properties and Corrosion Resistance of B4C/Al 4 C/Al Composites Via Forming "Tio2-Al" 2-Al" Interfacial Layer

Preparation of B4Cp/Al Composites via Selective Laser Melting and Their Tribological Properties

Design and Fabrication of a Nanoamorphous Interface Layer in B4C/Al Composites to Improve Hot Deformability and Corrosion Resistance

Developing nacre-inspired laminate-reticular 2024Al/B4C composites with high damage resistance by adjusting compositional wettability

Simultaneously Increasing the Mechanical Properties and Corrosion Resistance of B4C/Al Composites Via Forming “tio2–al” Interfacial Layer

Improvement on Mechanical Property of B4C/Al Composites by Addition of Ti Through Interfacial Reaction

Wetting behavior of Al on the surface of SiC textured by nanosecond laser

Rapid Preparation of B4Cp/Al Composites with Homogeneous Interface Via Ultrasound Assisted Casting Method

Understanding wetting mechanism of pure Cu on C/C composites modified by chromium carbide

High damage-tolerance bio-inspired B4C/2024Al composites with adjustable mechanical performance by tuning ceramic thickness

Theoretical and experimental investigation on superhydrophobic structure fabricated by femtosecond laser on alumina ceramics

Superhydrophobic Surface Preparation and Wettability Transition of Titanium Alloy with Micro/Nano Hierarchical Texture

Microstructure and Wear Resistance of TiCp/Ti6Al4V Composite Coatings by Follow-Up Ultrasonic-Assisted Laser Additive Manufacturing

Interfacial Reactions and Mechanical Properties Studies of C-Coated and C/B4C Duplex-Coated SiC Fiber-Reinforced Ti2AlNb Composites

Enhanced Ductility of B4C/Al Composites by Controlling Thickness of Interfacial Oxide Layer Through High Temperature Oxidation of B4C Particles

Using in-situ conversed nano SiC to bond UHTC particles and construct anti-ablation coating

Laser Surface Modification of Aluminium Alloy AlMg9 with B4C Powder

Enhanced Ductility by Controlling Thickness of Interfacial Oxide Layer in B4c/Al Composites