The Effect of μ-Limestone Additions on the Mechano-Chemical and Microstructural Properties of Slag and Binary Slag/Ground Fly Ash Alkaline-Activated Binders
Francisco Javier Vázquez-Rodríguez,Lucio Guillermo López-Yépez,Nora Elizondo-Villarreal,Ana María Guzmán-Hernández,Lauren Yolanda Gómez-Zamorano,Edén Amaral Rodríguez-Castellanos
DOI: https://doi.org/10.3390/ma17235940
IF: 3.4
2024-12-05
Materials
Abstract:An alternative approach to reducing the clinker factor, i.e., worldwide CO2 emissions resulting from the production of composite cement, is to replace these materials with supplementary aluminosilicate-based materials that promote the formation of alkali-activated cements, whose elevated temperature resistance, limited permeability, strong binding properties, excellent durability, high chemical corrosion resistance, confinement of toxic waste, and environmentally low impact have attracted a lot of attention in the cement industry. The principal aluminosilicate-based supplementary materials (SCMs) used in the cement industry are fly ash and blast-furnace slag. Recently, limestone has been proposed for use in alkali-activated cement to improve mechanical resistance and promote nucleation sources for the hydration of hybrid gels. In the current research work, the effect of 5 and 10 wt% limestone additions to slag and fly ash/slag alkali-activated cements with NaOH-4M was studied to evaluate the mechano-chemical and microstructural properties of alkali-activated cement. The effect of limestone was studied using mechanical resistance, XRD, FTIR, SEM-EDS, and calorimetry methods. The XRD, FTIR, and SEM-EDS results demonstrated the formation of portlandite Ca(OH)2 after the activator solution's reaction with limestone. The limestone's dissolution in Ca2+ contributes to hybrid gel formation ((N, C)-A-S-H, N-A-S-H, and C-A-S-H), resulting in compressive strength higher than 20 MPa, the recommended resistance for commercial cement.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering