Anomalous Conductivity of Glassy Li2O:4MnO2-x:4B2O3 During Heat Treatment
Sumin Wang,Xuejie Huang,Cailu Xu,Ji Liang,Liquan Chen,Dehai Wu
DOI: https://doi.org/10.1142/9789812791979_0029
IF: 3.699
2000-01-01
Solid State Ionics
Abstract:Solid State Ionics, pp. 209-213 (2000) No AccessAnomalous Conductivity of Glassy Li2O:4MnO2-x:4B2O3 During Heat TreatmentSumin Wang, Xuejie Huang, Cailu Xu, Ji Liang, Liquan Chen, and Dehai WuSumin WangLaboratory for Solid State Ionics, Institute of Physics, Chinese Academy of Sciences, P.O. Box: 603, Beijing, 100080, ChinaState Key Laboratory of Automotive Safety and Energy, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China, Xuejie HuangLaboratory for Solid State Ionics, Institute of Physics, Chinese Academy of Sciences, P.O. Box: 603, Beijing, 100080, China, Cailu XuState Key Laboratory of Automotive Safety and Energy, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China, Ji LiangState Key Laboratory of Automotive Safety and Energy, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China, Liquan ChenLaboratory for Solid State Ionics, Institute of Physics, Chinese Academy of Sciences, P.O. Box: 603, Beijing, 100080, China, and Dehai WuState Key Laboratory of Automotive Safety and Energy, Department of Mechanical Engineering, Tsinghua University, Beijing 100084, Chinahttps://doi.org/10.1142/9789812791979_0029Cited by:0 (Source: Crossref) PreviousNext AboutSectionsPDF/EPUB ToolsAdd to favoritesDownload CitationsTrack CitationsRecommend to Library ShareShare onFacebookTwitterLinked InRedditEmail Abstract: The conductivity of glassy material Li2O:4MnO2-x:4B2O3, prepared by quenching the melt in air has been studied by impedance spectroscopy and X-ray diffraction. Two kinds of conductivity anomalies have been observed around the crystallization temperature. One conductivity anomaly is observed for the pristine glass specimen annealed at 400°C in air, the conductivity increases quickly at first and then declines slowly. While the conductivity for specimen annealed in argon decreases slightly with annealing time. Moreover, the conductivity of specimen annealed in air is one order of magnitude higher than that of specimen annealed in argon. This phenomenon is due to the effect of the oxygen partial pressure on the concentration of small polaron. The other conductivity anomaly is observed for the annealed specimens heat-treated at 420°C. It was found that the conduction process is rather complicated for the glassy LiMnBO annealed for 150 minute. Below 200°C, the conductivity obeys Arrhenius relation. Above 350°C, the crystallization of MnBO3 makes the decrease of conductivity by one order of magnitude. In between the conductivity is enhanced by the redistribution of free volume. Keywords: ConductivityConcentration of small polaronCrystallizationLithium manganese borate glass FiguresReferencesRelatedDetails Recommended Solid State IonicsMetrics History KeywordsConductivityConcentration of small polaronCrystallizationLithium manganese borate glassPDF download