Nanodiamond-Structured Zinc Composite Coatings with Strong Bonding and High Load-bearing Capacity

Shikha Awasthi,Blanca Prior Palomero,Ankur Srivastava,Sankar Selvaraj,Sarvesh Kumar Pandey

DOI: https://doi.org/10.1039/d3na00809f

IF: 5.598

2024-01-07

Nanoscale Advances

Abstract:The aerospace and automotive industries find that relying solely on the intrinsic resistance of alloys is inadequate to safeguard aircraft and automotive structural components from harsh environmental conditions. While it is difficult to attribute accidents exclusively to coating failure due to the involvement of multiple factors, there are instances where defects in the coating initiate a wear or degradation process, leading to premature and unplanned structural failures. Metallic coatings have been introduced to protect the aircraft mainly from wear due to the extreme temperatures and moisture they get exposed to during their service life. The bare metallic coatings have a limited lifespan and need to be replaced frequently. Herein, the strength and wear resistance of zinc (Zn) coating is enhanced using varying concentrations of diamond particles as an additive in the Zn matrix (Zn-D). The dispersion strengthening mechanism is attributed to the high hardness (70 HRC), reduced friction-of-coefficient (0.21) and dissipation energy (4.6 × 10-4 J) of electrodeposited in Zn-D7.5 (7.5 g/l of diamond concentration) composite coating. Moreover, enhanced wear resistance with minimum wear volume (1.12 × 10-3 mm3) and wear rate (1.25 × 10-3 mm3/Nm) of Zn-D7.5 composite coating offered perfect blending of diamond with Zn. The improved hardness and wear resistance for Zn-D7.5 (optimum 7.5 g/l diamond concentration) is due to the steadiness between well-dispersed diamonds in Zn and enrichment in load-bearing ability due to the incorporation of diamond particles. Electronic structure calculations on the zinc-diamond composite models (two configurations adopted) have been performed using the density functional theory (DFT) approach and the in-silico studies appeared to facilitate meaningful and evocative outcomes. The Zn-doped diamond (C10@Zn) without hydrogen (H) atoms (binding energy: 418 kcal/mol, i.e. showing endothermic reaction and thermodynamically not favourable) was detected to be more stable than the Zn-doped diamond (C10H16@Zn) consisting of hydrogen (H) atoms (binding energy: -33.3 kcal/mol, i.e. showing exothermic reaction and thermodynamically preferable). Thus, the composite coating of zinc and diamond can be a pioneering candidate for the aerospace and automotive industries.

materials science, multidisciplinary,nanoscience & nanotechnology,chemistry