Abstract:In this investigation, ultrasonic-assisted soldering at 260 °C in air produced high strength and high melting point Cu connections in 60 s using Ni foam reinforced Sn composite solder. Systematically examined were the microstructure, grain morphology, and shear strength of connections made with various porosities of Ni foam composite solders. Results shown that Ni foams as strengthening phases could reinforce Sn solder effectively. The addition of Ni foam accelerated the metallurgical reaction due to great amount of liquid/solid interfaces, and refined the intermetallic compounds (IMCs) grains by ultrasonic cavitation. The joints had different IMCs by using Ni foam with different porosity. Layered (Cu,Ni) 6 Sn 5 and (Ni,Cu) 3 Sn 4 phases both existed in Cu/Ni60-Sn/Cu joint while only (Cu,Ni) 6 Sn 5 IMCs grew in Cu/Ni98-Sn/Cu joint. As ultrasonic time increasing, Ni skeletons were dissolved and the IMCs were peeled off from substrates and broken into small particles. And then, the IMCs gradually dissociated into refined particles and distributed homogeneously in the whole soldering seam under cavitation effects. Herein, the Cu/Ni60-Sn/Cu joint ultrasonically soldered for 60 s exhibited the highest shear strength of 86.9 MPa, as well as a high melting point about 800 °C for the solder seam composed of Ni skeletons and Ni-Cu-Sn IMCs. The characterization indicated that the shearing failure mainly occurred in the interlayer of the soldering seam. The homogeneous distributed granular IMCs and Ni skeletons hindered the crack propagation and improved the strength of Cu alloy joints.

Direct soldering of TiO2 nanotubes in air by ultrasonic vibration

Nanojoint Formation Between Ceramic Titanate Nanowires and Spot Melting of Metal Nanowires with Electron Beam

Bonding mechanism of ultrasonically soldered silica glasses using tin-titanium solder filler

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Improved shear property of Sn-3.0Ag-0.5Cu/Ni micro solder joints under thermal shock between 77 K and 423 K by adding TiO2 nanoparticles

Selenium Nanotubes Synthesized by A Novel Solution Phase Approach

Application of Ultrasonic Power in Forming Sn58Bi/Cu Solder Joints with Trace Si3N4 Nanowire Doping

Free-standing TiO(2) nanotube arrays made by anodic oxidation and ultrasonic splitting.

Ultrasonic-assisted wetting and soldering of AlN ceramic by using a nonactive solder (Sn9Zn) in air

Microstructure and shear property of Ni-coated carbon nanotubes reinforced InSn-50Ag composite solder joints prepared by transient liquid phase bonding

Sn-enhanced high-temperature reliability of Cu/Nano-Ag/Cu joint via transient-liquid-phase bonding

Bonding mechanism in ultrasonic-assisted soldering of ZrO2 and 304 stainless steel using a micro-alloyed active solder alloy

Ultrasonic-Induced Synthesis of Ceo2 Nanotubes

Microstructure evolution and grain refinement of ultrasonic-assisted soldering joint by using Ni foam reinforced Sn composite solder

Avoiding degradation and increasing joint strength of Al alloys by rapid ultrasonic soldering at low temperature

Combination of chemical vapor deposition and thermal growth methods for facile synthesis of tin oxide-doped multiwalled carbon nanotubes

Synthesis and Study of SrTiO3/TiO2 Hybrid Perovskite Nanotubes by Electrochemical Anodization

Low temperature bonding mechanism of porous Si3N4 ceramics by Sn9Zn solder in ultrasonic-assisted soldering

Fast low-temperature ultrasonically soldering porous Si3N4 ceramics in the air

Ultrasonic semi-solid coating soldering 6061 aluminum alloys with Sn-Pb-Zn alloys

Sonoelectrochemical synthesis of CdSe nanotubes.