Abstract:Introduction. Searching for new methods of making less energy-intensive materials by reducing their cost, adding local raw materials and industrial waste to the mineral resource base, as well as developing efficient production technologies is a relevant problem of the construction industry. A clinker-free technology for the manufacture of hydraulic binders will partially replace resource-intensive Portland cement in construction and help to solve these problematic issues to a certain extent and boost the environmental safety at the global level. The proposed binders, based on principles of structurization in alkaline systems as a combination of sequential and parallel physical and chemical transformations due to the contact interaction between fine powders of aluminosilicate nature and cations of alkali metals, contribute to the formation of strong and durable composites. Materials and methods. The study of energy dispersive microanalysis of components of the binder system was performed using the QUANTA 3D scanning electron microscope; dynamic light scattering was employed to study the particle granulometry with the help of the HORIBA analyzer. The strength characteristics of the binder systems “aspiration dust – bentonite – Na2O∙SiO2” were determined according to GOST 30744-2001 using Testometric FS150AT testing machine. Results. Electron microscopic analysis showed that particles of aspiration dust larger than 200 microns and smaller than 100 microns have a similar oxide composition, with a predominance of oxides of calcium, silicon, aluminum and carbon. The chemical composition of bentonite confirms the aluminosilicate nature. An increase in the physical and mechanical properties of specimens of the systems “aspiration dust – bentonite – Na2O∙SiO2” has been identified; it is the addition of higher dispersion bentonite that contributes to the dense packing of grains due to the volume-wise redistribution of particles, which positively affects the pore structure and water resistance of the cement stone. Conclusions. The results of the study have proven the new prospects for the alkaline activation of complex powders made of cement industry waste and bentonite clay; the characteristics and dependencies, obtained by the authors, will allow using the proposed technology in construction.

Heat-Resistant Ceramic Concrete Based Upon Diatomite. 1. Synthesis and Study of Artificial Ceramic Binders Based Upon Diatomite

Cement-Free Refractory Concretes. Part 6. Comparative Evaluation of Natural (Clay) and Artificial Ceramic Binders (HCBS)

Mechanical and thermal insulation performance of waste diatomite cement mortar

Ceramic Thermal Insulator Based on Diatomite Obtained by Starch Consolidation Casting

Design, Characterization, and Incorporation of the Alkaline Aluminosilicate Binder in Temperature-Insulating Composites

Mechanical properties of low calcium alkali activated binder system under ambient curing conditions

Design and characterization of iron–calcium–aluminium–silicate–hydrate as low-temperature binder

Purification and Carbonation for High Loss and Low-Grade Diatomite in Inner Mongolia

Effect of addition diatomite powder on mechanical strength, elevated temperature resistance and microstructural properties of industrial waste fly ash-based geopolymer

Preparation and Thermal Performance Testing of Diatomite-Modified Asphalt Pavements

Preparation and Investigation of a Heat-Resistant Binder with a Metakaolin Additive Made of Aral Sea Raw Materials

Strength, Shrinkage and Early Age Characteristics of One-Part Alkali-Activated Binders with High-Calcium Industrial Wastes, Solid Reagents and Fibers

Binders for pressed products based on phosphogypsum waste

Investigation of the properties of alkaline binding materials with the addition of fine bentonite

Usage Possibilities of Diatomite in the Concrete Production for Agricultural Buildings

A novel composite binder design for direct ink writing alumina-based ceramics with enhanced strength at low sintering temperature

Cement Substitution in High-Temperature Concrete

Thermally-treated asbestos-cement wastes as supplementary precursor for geopolymeric binders: CO 2 emission and properties

Alkali-Activated Binary Binders with Carbonate-Rich Illitic Clay

Morphology and thermal stability of BR/clay composites prepared by a new method

The Effect of Diatomite's Chemical on High Temperature Performance of Asphalt