Reducing applied field in NBT-based high energy-storage ceramics via B-site entropy regulation

Min Chen,Yongping Pu,Lei Zhang,Bo Wang,Fangping Zhuo,Xiaolei Gao,Till Frömling

DOI: https://doi.org/10.1016/j.cej.2023.145386

IF: 15.1

2023-08-28

Chemical Engineering Journal

Abstract:Recently, ceramics have raised much interest for high-power and high-energy capacitors applications. The W rec (recoverable energy density) generally increases with applied E (electric field). Thus, the high-field properties must be excellent. Due to enhanced degradation, lower fields would be, nevertheless, preferable. We proposed a novel strategy to improve simultaneously the tolerance factor and configurational entropy based on the composition of (1 − x )NBT- x BMZNT. This leads to a high W rec (1.21 J/cm 3 ) and a high efficiency η (86%) under a low E of 100 kV/cm, which is superior to other ceramic components. The discharge test furthermore illustrates a high discharge W d (>0.8 J/cm 3 ) over the temperature range from 20 to 160 °C caused by the high permittivity ∼2700 ± 15% from 50 °C to 370 °C. XRD and Raman results present that BMZNT can fully diffuse into the NBT lattice when x < 0.18. Furthermore, BMZNT addition also increases the lattice symmetry and volume. Modulus M ′′ and Piezo-Force-Microscopy (PFM) results demonstrate that sheetlike domains gradually become fragmented to PNRs (polar nanoregions), leading to their rapid response to the applied E . Our work will provide a entropy regulation strategy to reduce the applied field without compromising the energy-storage performance.

engineering, chemical, environmental