Abstract:The effect of nitrogen content on the formation of an equiaxed solidification structure of Fe-16Cr steel was investigated. Moreover, two different kinds of refractory materials, i.e., alumina and magnesia, were employed to control the type of oxide inclusion. The characteristics of TiN(-oxide) inclusions were quantitatively analyzed in both molten steel and solidified samples. When the melting was carried out in the alumina refractory, the grain size continuously decreased with increasing nitrogen content. However, a minimum grain size was observed at a specific nitrogen content (approx. 150 ppm) when the steel was melted in the magnesia refractory. Most of the single TiN particles had a cuboidal shape and fine irregularly shaped particles were located along the grain boundary due to the microsegregation of Ti at the grain boundary during solidification. The type of TiN-oxide hybrid inclusion was strongly affected by the refractory material where Al2O3-TiN and MgAl2O4-TiN hybrid-type inclusions were obtained in the alumina and magnesia refractory experiments, respectively. The formation of oxide inclusions was well predicted by thermochemical computations and it was commonly found that oxide particles were initially formed, followed by the nucleation and growth of TiN. When the nitrogen content increased, the number density of TiN linearly increased in the alumina refractory experiments. However, the number of TiN exhibits a maximum at about [N] = 150 ppm, at which a minimum grain size was obtained in the magnesia refractory experiments. Therefore, the larger the number density of TiN, the smaller the primary grain size after solidification. The number density of TiN in the steel melted in the magnesia refractory was greater than that in the steel melted in the alumina refractory at given Ti and N contents, which was due to the lower planar lattice disregistry of MgAl2O4-TiN interface rather than that of Al2O3-TiN interface. When ∆TTiN (= difference between the TiN precipitation temperature and the liquidus of the steel) was 20 K to 40 K, the number density of effective TiN was maximized and thus, the grain size was minimized after solidification. Finally, although most of the TiN particles were smaller than 1 μm in the molten steel samples irrespective of the nitrogen content, TiN particles larger than 10 μm were observed in the solidified samples when the nitrogen content was greater than 150 ppm. The growth of TiN particles during melting and solidification was well predicted by the combinatorial simulation of the ‘Ostwald ripening model’ based on the Lifshitz–Slyozov–Wagner theory in conjunction with the ‘Diffusion controlled model’ using Ohnaka’s microsegregation equation.

ISIJ International, Vol. 47 (2007), No. 8, pp. 1082–1089

Control of TiN precipitation behavior in titanium-containing micro-alloyed steel

Synergistic Effect of Nitrogen and Refractory Material on TiN Formation and Equiaxed Grain Structure of Ferritic Stainless Steel

Precipitation Behavior of TiN During the Solidification of High-Titanium Steel

Thermodynamic and Kinetic Analysis of TiN Precipitation in Nickel-Based Superalloys During Solidification

Evolution of chemical, structural, and mechanical properties of titanium nitride thin films deposited under different nitrogen partial pressure

Formation of TiN Inclusions During Solidification of Titanium Micro-Alloyed Steel: Modeling With ChemAppPy

Distribution and precipitation mechanism of TiN in industrial pure iron bloom

Thermodynamic Analysis of Titanium Removal from Molten iron Smelted with Large Amounts of Sodium Additives

First Principles Calculations of the Influence of Nitrogen Content on the Mechanical Properties of Α-Ti

STRUCTURE AND MECHANICAL PROPERTIES OF AUSTENITIC Cr – Ni – Ti STEELS AFTER HIGH-TEMPERATURE NITRIDING

Interaction between Silicon and Titanium in Molten Steel

Effect of Solid Solution Elements on Solubility Products of Carbides and Nitrides in Austenite: Thermodynamic Calculations

Control of Coarse Precipitates of Titanium Nitride in High-Strength Low-Alloy Steel

Effect of Magnesium Content on Precipitation Behavior of TiN-Containing Inclusions in High-Titanium High-Strength Steel

Comparison study on mechanical properties of powder metallurgy titanium materials with nitrogen solutes and TiN dispersoids

In Situ Observation of the Precipitation, Aggregation, and Dissolution Behaviors of TiN Inclusion on the Surface of Liquid GCr15 Bearing Steel

Simulation of Oxygen and Nitrogen Removal from Steel by Means of Titanium and Aluminum

Effect of aluminum, titanium or silicon addition on nitrogen removal from molten iron

Ionized Physical Vapor Deposition of Titanium Nitride: Plasma and Film Characterization

Isotope Exchange Measurements of the Interfacial Reaction Rate Constant of Nitrogen on Fe-Mn alloys and an Advanced High-Strength Steel