In-Situ Scanning Transmission X-Ray Microscopy Studies of MnO2-Based Supercapacitor Electrodes
Haytham Eraky,Chunyang Zhang,Drew Higgins,Adam P. Hitchcock
DOI: https://doi.org/10.1149/ma2023-02552713mtgabs
2023-01-01
Abstract:Supercapacitors (SCs) as energy storage devices provide higher energy density than conventional capacitors and higher power density than batteries 1 . Understanding how charge is efficiently stored in the electrodes or across the electrolyte/electrode interface is key to developing advanced SC electrodes. Scanning transmission x-ray microscopy (STXM) studies 2 have been used to investigate MnO 2 based supercapacitor electrodes using a novel three-electrode based in-situ flow electrochemical device ( Fig. 1 ) 3, 4 . Near-edge X-ray absorption fine structure (NEXAFS) spectra of MnO 2 films in-situ deposited and subjected to several different electrochemical processes were measured with high spatial resolution at the Mn L 3 and O K edges ( Fig. 2 ) at both working electrode (WE) and counter electrode (CE) regions. In this work, the redox state changes associated with pseudocapacitance during charging/discharging processes in a potential window of -0.5 V Au to +0.9 V Au (+0.1 V RHE to +1.5 V RHE ) have been investigated. The spectroscopic data and quantitative chemical mapping by in-situ STXM measurements demonstrated that an as-electrodeposited MnO 2 film was reduced to both Mn 3+ and Mn 2+ oxidation states through a reversable Mn 4+ ↔ Mn 3+ /Mn 2+ redox reaction. A significant change from a quasi-uniform MnO 2 film to a dendritc MnO 2 structure was observed during discharging at +1.5 V RHE ( Fig. 3, Fig. 4 ) corresponding to redeposition of Mn 2+ dissolved into electrolyte during the reduction process 5 . I n-situ STXM measurements at the CE showed there is deposition of MnO 2 during the reduction reaction (charging process) at +0.1 V RHE . Mn L 3 features of Mn 2+ appeared in the electrolyte region during the reduction process and disappeared during the oxidation process, confirming the dissolution/redeposition mechanism. We have developed a novel and versatile platform for in situ studies of electrochemical processes, including supercapacitors, batteries, and electro-catalysts 3, 4 . References A. G. Olabi, Q. Abbas, A. Al Makky, and M. A. Abdelkareem, Energy, 248 123617 (2022). K. V. Kaznatcheev, C. Karunakaran, U. D. Lanke, S. G. Urquhart, M. Obst, and A. P. Hitchcock, Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment, 582 (1), 96-99 (2007). A. P. Hitchcock, C. Zhang, H. Eraky, L. Shahcheraghi, F. Ismail, and D. Higgins, Microscopy and Microanalysis, 27 (S2), 59-60 (2021). C. Zhang, N. Mille, H. Eraky, S. Stanescu, S. Swaraj, R. Belkhou, D. Higgins, and A. Hitchcock, (2023). T.-H. Wu, Y.-Q. Lin, Z. D. Althouse, and N. Liu, ACS Applied Energy Materials, 4 (11), 12267-12274 (2021). Figure 1