Construction of a Three-Dimensional Interpenetrating Network Sponge for High-Efficiency and Cavity-Enhanced Solar-Driven Wastewater Treatment

Xinling Wang,Zehao Li,Yi Wu,Hongran Guo,Xiaoli Zhang,Yuxin Yang,Haibo Mu,Jinyou Duan

DOI: https://doi.org/10.1021/acsami.0c21690

2021-02-25

Abstract:It is well known that the photothermal conversion performance of solar-driven interfacial water evaporation systems is known to have a stronger photothermal conversion performance than suspended water evaporation systems due to their relatively strong ability to suppress overall heat loss. Natural polymer chitosan and gelatin can form a three-dimensional interpenetrating network (IPN) sponge to provide an interface for water evaporation due to strong hydrogen bonding and electrostatic attraction interaction. However, the lack of effective light absorption, the intrinsic short lifetime, and the poor photothermal conversion greatly compromise their steam generation performance. Here, we fabricated a chitosan/gelatin-based IPN sponge incorporated with melanin-coated titania hollow nanospheres () as a solar thermal converter, which is designed to exhibit a unique cavity structure and vertical channels. The cavity structure of melanin-coated titania acts as a solar thermal transducer, while the chitosan/gelatin-based IPN sponge acts as a single-pass water pump. A water hyacinth-inspired evaporation system shows outstanding steam generation performance, and the highest steam generation rate was 3.17 kg m^–2 h^–1 under a 2.5 sun illumination because of the cavity enhancement effect, far above TiO₂ particles and reported photo-thermal conversion materials. More importantly, the embedding of MPT-h nanoparticles in the IPN sponge effectively inhibits the growth of bacteria in the vertical channels, resulting in an antibacterial solar-driven water evaporator. This advanced sponge provides a cost-effective and practical sustainable energy technique for solar-driven wastewater treatment.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c21690?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c21690</a>.Schematic diagram of the sponge fabrication process (Figure S1); stability, porosity and capillarity of the sponge (Notes S1); weight loss ratio of the sponge (Figure S2); swelling ratio, saturated water content, and calculated water transport rate of the sponge (Figure S3); determination of pH_pzc (Figure S4); schematic illustration of the formation mechanism of the sponge (Figure S5); SEM image, light absorption, and reflectance spectra of the sponge (Figure S6); surface temperature of different samples (Figure S7); infrared radiation thermal images of different samples (Figure S8); mass change of evaporated water and the actual evaporative efficiency of the sponge (Figure S9); mass change of evaporated water and the actual evaporative efficiency in the sponge with different MPT-h contents (Figure S10); duration test of the sponge (Figure S11); calculation of steam generation efficiency (Table S1); the relevant results of the current solar-driven steam generation system experiments (Table S2); roof-solar still (Figure S12); infrared images of the (Figure S13); antibacterial property of sponges (Figure S14); representative TiO₂ materials with their antibacterial performances (Table S3); and water evaporation rate of the sponge with different thicknesses (Notes S2) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c21690/suppl_file/am0c21690_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology