Slurry Erosive Wear Behaviour of TiO 2 – 30 wt % Inconel-718 Plasma Sprayed Coatings on Al 6061 Substrate CONTROL ID : 2411214 CURRENT TOPIC : Surface Engineering
Ramesh Chinnakurli Suryanarayana,Suresh Kumar,Aditya Nagaraj,Vishwadeep,Zulfiqar Khan
2016-01-01
Abstract:The present investigation is aimed at developing plasma sprayed TiO2 – 30 wt% Inconel-718 coatings on Al6061 substrate and to evaluate its microstructure, microhardness and slurry erosive wear resistance. TiO2 – 30 wt% Inconel-718 powders were thermally sprayed on Al6061 substrate by Air Plasma Spray process. An average particle size of 50μm was adopted to achieve dense and uniform coatings of thicknesses 100 μm and 200μm. The developed coatings were subjected to microstructural studies, microhardness and slurry erosive wear tests in 3.5% NaCl solution with sand as erodent. Microstructural studies reveal dense coatings of TiO2 – 30 wt% Inconel-718 coating with good bond and minimal porosities. The slurry erosive wear resistance of developed coatings are superior when compared with that of uncoated Al6061 substrate under identical test conditions. Introduction Wear caused by solid particle erosion has been a matter of concern in the recent years, one such phenomenon is slurry pot erosion. The erosion wear depends on parameters like material properties, impact angle, velocity, fluid properties, and particle size. Q.B. Nguyen[1] noted that the type of erosion is different for brittle and ductile materials and further showed that the erosion rate of stainless steel SUS304 increased over increase in testing time and impact velocity. M.Lindgren [2] revealed that the severity of the erodents with respect to wear was same for titanium as well as 316L stainless steel and indicated that the particle properties that determine their erosivity are the same for both ductile metals, titanium and stainless steel. Girish R. Desale [3] observed that a threshold kinetic energy of impacting particle existed which resulted in change in wear rate at a particular particle size. Conducted in a slurry pot tester with erodents of different size and shape, it was observed that the erodents damaged the surface of the substrate by several mechanisms like microcutting and crater formation. The substrate was subjected to significant weight loss due to erosion and was dependent on the kinetic energy of the erodent particles and also their shape. Slurry pot tester is used to test wear resistant materials and enables testing with high speeds upto 20m/s with large particle size of 10mm of that of the slurry, but the literature reveals that increase in particle size decreases the number of particles suspended in the slurry mixture as a result the kinetic energy and wear of the particle increases per impact proportion and vice versa. Erosion also depends on environmental conditions when it becomes hostile and corrosive in nature. The most commonly used slurry mixture is quartz/alumina sand with water and the microstructure characterization of the erosion caused by these mixture reveals two different erosion regimes; the plastic deformation mechanism dominated at high impact angles and the Cutting/plowing mechanism dominated at low impact angles. Girish R. Desale [4] carried out the erosion wear tests on seven different ductile materials at normal impact condition and noted that the wear at normal impact condition is a strong function of hardness ratio of erodent and target materials. In the present work, slurry erosive wear behavior, its microstructure and microhardness of TiO2 30wt% Inconel-718 coatings developed on Al6061 substrate by plasma spraying are studied. EXPERIMENTAL DETAILS Among several thermal spray coating methods, atmospheric plasma spraying (APS) is an efficient method for material deposition and is primarily used in forming protective coatings on a variety of metallic and ceramic substrates Fig. 1: Cross sectional micrograph indicating 100 microns Fig. 2: Micrograph of the coated specimen indicating splats In the present work, Al6061 is used as the substrate and TiO2 30wt% Inconel-718 powder is used as coating material with the particle size varying from 5μm to 50 μm. Coating is applied using plasma spray coating technique. The substrate is cleaned to remove all dust particles and grit blasted before plasma spraying to create enough surface roughness to ensure good bond between substrate and coating. Then a layer of bond coat is applied on the substrate. TiO2 30wt% Inconel-718 powder is melted and ionized to plasma state and then sprayed using a gun along with hydrogen and argon gas onto the base metal from a standoff distance of 10 cm. The voltage and current of 48 volts and 500 amps respectively were maintained during coating. The flow rates of hydrogen and Argon are 0.6 lpm and 30 lpm respectively and that of powder is 120 gm/min. Coatings of thickness 100 and 200 μm were developed. Figure 1 shows the cross sectional SEM micrograph for 100 μm thickness and Figure 2 shows the SEM micrograph indicating splats. It can be noticed that the coating is uniform and porosity is less. Vickers’s hardness tester was used to measure the micro hardness and a load of 200 g was applied for 10 seconds. The test was conducted at different locations and the average hardness value was calculated. Wear test of TiO2-30wt% Inconel-718 coating on Al6061 substrate was conducted using slurry erosive wear testing machine. The effect of Speed, Particle Size and Slurry Concentration were studied. RESULTS AND DISCUSSION The micro hardness test yielded the hardness values for 100 and 200 μm coating thickness in terms of Vicker’s Hardness Number as shown in Figure 3. Fig. 3: Coating Thickness vs VHN Figures 4, 5 and 6 show the effect of Slurry Concentration, Speed and Particle size respectively on weight loss which is a measure of wear. From these figures, it can be observed that with increase in concentration of the sand in the slurry, increase in rotational speed of the specimen and increase in sand particle size, wear of the specimen increases but when compared to the coated specimen uncoated specimen wears out more. Wear of 200 μm coating thickness is least among the three. Reduction in wear of coated specimen may be attributed to the presence of hard ceramic Titanium dioxide on the surface of Al 6061. Fig. 4: Effect of Sand concentration Fig. 5: Effect of Speed Fig. 6: Effect of Particle size CONCLUSIONS Plasma spray coating of TiO2 – 30 wt% Inconel-718 on Al6061 substrate helped to improve wear resistance. With increase in Slurry Concentration, Speed and Sand Grain Size, wear of test specimen increases. Wear of 200 μm thick coating on Al6061 is the least compared to uncoated and 100 μm thick coatings. REFERENCES 1. Q.B. Nguyen , C.Y.H. Lim , V.B. Nguyen , Y.M. Wan , B. Nai , Y.W. Zhang , sM. Gupta,Slurry erosion characteristics and erosion mechanisms of stainless steel, Tribology International , 2014, 79, 1-7 2. M. Lindgren , J.Perolainen , Slurry pot investigation of the influence of erodent characteristics on the erosion resistance of titanium, Wear,Vol 321, 30 Dec 2014, Pages 64-69 3. Girish R. Desale, Bhupendra K. Gandhi , S.C. Jain, Particle size effects on the slurry erosion of aluminium alloy (AA 6063), Wear, Volume 266, Issues 11–12, 30 May 2009, Pages 1066– 1071 4. Girish R. Desale, Bhupendra K. Gandhi , S.C. Jain, Slurry erosion of ductile materials under normal impact condition, , Wear 264 (2008) 322–330