Study of low manganese solution loss HAMO@ZrO 2 via experimental and theory methodology

Feng Xue,Jinyan Qian,Xiaoxian Zhang,Zhijun Xu,Shengui Ju

DOI: https://doi.org/10.1016/j.desal.2024.117290

IF: 11.211

2024-01-13

Desalination

Abstract:Lithium, being the lightest element in nature, has garnered attention for its potential to recover Li + from brine. One of the promising materials in this context is spinel-structured lithium manganese oxide. Herein, a novel ZrO 2 shell/Al 3+ doped H 1.6 Mn 1.6 O 4 core lithium ion sieve, namely, HAMO@ZrO 2 , was successfully prepared. XRD, SEM, HR-TEM, and XPS were used to characterize the morphological properties and crystal structure of HAMO@ZrO 2 . The equilibrium adsorption capacity ( Q e ) of HAMO@ZrO 2 was found to be 36.89 mg·g −1 . Furthermore, desorption equilibrium was achieved within 40 min when LAMO@ZrO 2 was immersed in a 0.05 mol·L −1 H + solution, resulting in reduced manganese dissolution from 2.38 % to 1.4 %. The structural stability of HAMO@ZrO 2 was explained using density functional theory (DFT), where the total structure energy was carefully estimated. Even after ten adsorption-desorption cycles, the Li + adsorption capacity of HAMO@ZrO 2 was sustained at 29.69 mg·g −1 . The dissolution loss of Mn 2+ ( R Mn2+ ) was less than 2 %, demonstrating the effective regeneration property of HAMO@ZrO 2 . In addition to its impressive properties, HAMO@ZrO 2 exhibited high selectivity for Li + over hetero-atoms in artificial brine. These findings make HAMO@ZrO 2 a promising candidate for Li + recovery applications.

engineering, chemical,water resources