Research on the Microstructure and Properties of Al Alloy/Steel CMT Welding-Brazing Joints with Al–Si Flux-Cored Welding Wires

Haodong Liu,Juan Pu,Mingfang Wu,Chao Zhang,Jiawei Rao,Weimin Long,Yuanxun Shen
DOI: https://doi.org/10.3390/coatings13091590
IF: 3.236
2023-09-13
Coatings
Abstract:Al alloy/steel composite structures combine the advantage of a lightweight Al alloy and high-strength steel and are widely used in new energy vehicles, solar photovoltaic, and other fields. The main problems with the connection of an Al alloy and steel are poor weld formation and difficulty in controlling the thickness of the intermetallic compounds (IMCs) at the interface of the Al alloy and steel, which deteriorates the mechanical properties and corrosion resistance of the Al alloy/steel joints. Therefore, experiments on Al alloy/steel CMT (cold metal transfer, CMT) welding brazing were conducted by using AlSi5 and AlSi12 flux-cored welding wires as filler metals. The macro morphology, microstructure composition, tensile strength, and corrosion resistance of the Al alloy/steel joints were then analyzed. The mechanism of the Noclock flux on the wettability and spreadability of the Al–Si welding wire to a low-carbon steel surface was discussed and the formation behavior of the IMCs at the interface layer of the Al alloy/steel joints was clarified. The results showed that the NH4F and NH4AlF4 of the Noclock flux induced and accelerated the removal of oxide films on the surface of the Al alloy and Al–Si welding wire at a high temperature. It promoted the wettability and spreadability of the Al–Si welding wire, which resulted in the improvement of the Al alloy/steel joint formation. Under the CMT arc heat source, the Al–Si welding wire melted, and then a chemical metallurgical reaction occurred among the Al, Si, and Fe elements. The τ5-Al7.2Fe1.8Si phase formed preferentially near the Al alloy fusion zone while the θ-Fe (Al, Si)3 phase formed near the steel side. Actually, the interface reaction layer was composed of a double-layer compound including the τ5-Al7.2Fe1.8Si phase and θ-Fe (Al, Si)3 phase. Additionally, the IMC thickness of the Al alloy/steel joint with the AlSi12 flux-cored welding wire was 3.01 μm, which was less than that with the AlSi5 flux-cored welding wire, so its tensile strength was less but its corrosion resistance was superior. The main reason for the corrosion resistance of Al alloy/steel joints was the presence of a large amount of Al2O3, FeO, and Fe2O3 in the passive film.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
This paper attempts to solve several main problems in the welding of aluminum alloy and steel: 1. **Poor weld formation**: Since the surface of aluminum alloy is prone to form a stable oxide film, this will lead to the generation of inclusions during the welding process, which will damage the continuity and performance of the joint. 2. **Difficulty in controlling the thickness of interfacial intermetallic compounds (IMCs)**: A series of brittle Fe - Al intermetallic compounds will be generated between aluminum and steel, and these compounds will reduce the mechanical properties of the joint. 3. **Residual stress and cracks**: Due to the large difference in the linear expansion coefficients of aluminum and steel, residual stress and even cracks are likely to occur after welding. 4. **Corrosion problems**: The potential difference between aluminum and steel will lead to galvanic corrosion, affecting the safety of the structure. In order to overcome these problems, the paper studied the method of cold metal transfer (CMT) welding - brazing using Al - Si flux - cored wire. Specifically, the research focuses include: - **The influence of Noclock flux on the wettability and spreadability of Al - Si wire**: Analyze how Noclock flux improves the wettability and spreadability of Al - Si wire on the surface of low - carbon steel through experiments. - **Macroscopic morphology, microstructure composition, tensile strength and corrosion resistance**: Analyze the macroscopic morphology, microstructure, tensile strength and corrosion resistance of aluminum/steel joints. - **The formation behavior of interfacial intermetallic compounds**: Explore the formation mechanism of intermetallic compounds in the interfacial layer of aluminum/steel joints. Through these studies, the paper aims to achieve high - quality aluminum/steel connection at low cost and solve the problems of poor wettability and spreadability of welding wire and poor weld formation.