A cost-effective synthesis of heteroatom-doped porous carbon by sulfur-containing waste liquid treatment: As a promising adsorbent for CO2 capture
Xiaofei Guo,Guojie Zhang,Chenlei Wu,Jun Liu,Guoqiang Li,Yuqiong Zhao,Ying Wang,Ying Xu
DOI: https://doi.org/10.1016/j.jece.2021.105165
IF: 7.7
2021-04-01
Journal of Environmental Chemical Engineering
Abstract:<p>Based on efficiency and environmental concerns, the development of porous carbon from waste and biomass materials has attracted extensive attention as a novel approach. In this study, poplar sawdust was an inexpensive carbon precursor, sulfur-containing waste liquid (SCWL) was used as a modifier to turn waste into treasure, and potassium oxalate (K<sub>2</sub>C<sub>2</sub>O<sub>4</sub>) was a mild activator, successfully prepared N, S, O co-doped new porous activated carbon with excellent CO<sub>2</sub> capture performance. The heteroatom doping and pore structure can be controlled by using SCWL and K<sub>2</sub>C<sub>2</sub>O<sub>4</sub>, and adjusting the activation temperature. The best sample (PCSK-2-3-800) prepared with SCWL and K<sub>2</sub>C<sub>2</sub>O<sub>4</sub> showed excellent CO<sub>2</sub> adsorption performance, reaching 3.82 and 5.61 mmol/g under normal pressure at 25 and 0 °C, respectively. This is attributed to the synergy of porous structure and surface chemistry. The pore structure parameter results showed that K<sub>2</sub>C<sub>2</sub>O<sub>4</sub> promotes the development of activated carbon pore structure. The specific surface area, micropore volume and narrow micropore volume of PCSK-2-3-800 are 1418 m<sup>2</sup>/g, 0.55 cm<sup>3</sup>/g and 0.43 mL/g, respectively. The characterization results of FTIR and XPS showed that the addition of SCWL can successfully introduce heteroatoms into the carbon skeleton, and form CO<sub>2</sub>-philic active sites on the surface of the porous carbon. Both aspects promoted the adsorption of CO<sub>2</sub>. In addition, the PCSK-2-3-800 sample has a moderate adsorption heat of 27.13 kJ/mmol, good adsorption selectivity of CO<sub>2</sub> and N<sub>2</sub> is 13, and excellent recyclability, which is very promising for CO<sub>2</sub> separation or storage. This paper develops a sustainable scheme for the first-time using biomass and SCWL to develop a new solid carbon adsorbent, which provides useful information and inspiration for capturing CO<sub>2</sub>.</p>
engineering, chemical, environmental