Abstract:3D-printed carbon fiber composites hold significant potential in aerospace applications because of their lightweight, high strength and complex structure fabrication capabilities. However, additive manufacturing characteristics such as high porosity, anisotropy and continuous fiber content significantly affect the mechanical properties of printed parts. The aim of this study is to investigate the influence of hybrid printing of short and continuous carbon fibers on the mechanical properties and failure mechanisms of composites and to develop a model to predict elastic properties considering porosity. First, mechanical testing and characterization of short and continuous fiber reinforced polyamide (nylon) print filaments are performed. The results indicate that the elastic modulus and ultimate strength of continuous carbon fiber filaments reach 60 GPa and 1500 MPa, respectively, while the strength and elastic modulus of short carbon fiber filaments reach 60 MPa and 1 GPa, respectively. Then tensile specimens with different continuous fiber orientations and different continuous fiber placement sequences are printed and tested using a multi-material 3D printing technique. The specimens are characterized before and after testing using scanning electron microscopy and microscopy to assess the porosity and failure mechanisms of specimens with different configurations. The results show that the mechanical properties of the printed parts are much lower than those of the print filaments, which proves the serious negative impact of the material extrusion process on the mechanical properties of the printed structural parts. Finally, an analytical method for predicting the elastic behavior of printed composites is developed by introducing the porosity factor in the volume-averaged stiffness model. For continuous and short fiber filled composites with different fiber contents and printing orientations, the predicted results are in agreement with the experiments, and the prediction error is greatly reduced from 30% to less than 5%.

Mechanical and interfacial analysis of 3D-printed two-matrix continuous carbon fibre composites for enhanced structural performance

Experimental and Theoretical Studies on 3D Printed Short and Continuous Carbon Fiber Hybrid Reinforced Composites

An investigation into mechanical properties of a 3D printed two-matrix continuous fiber composites with multi-cavity structure

Investigation on the mechanical properties of 3D printed hybrid continuous fiber-filled composite considering influence of interfaces

Self-monitoring Continuous Carbon Fiber Reinforced Thermoplastic Based on Dual-Material Three-Dimensional Printing Integration Process

Interfacial behaviors of continuous carbon fiber reinforced polymers manufactured by fused filament fabrication: A review and prospect

Process evaluation, tensile properties, mathematical models, and fracture behavior of 3D printed continuous fiber reinforced thermoplastic composites

Integrated self-monitoring and self-healing continuous carbon fiber reinforced thermoplastic structures using dual-material three-dimensional printing technology

Mechanical properties and damage failure of 3D‐printed continuous carbon fiber‐reinforced composite honeycomb sandwich structures with fiber‐interleaved core

Layout design and mechanical behavior of 3D printed intralayer hybrid continuous carbon/glass fiber composites

Effect of infill density and reinforced perimeters on tensile properties and fracture mechanism of 3D printing carbon fiber–reinforced composite

Experimental analysis of 3D printed continuous carbon/glass hybrid fiber reinforced PLA composites: Revealing synergistic mechanical properties and failure mechanisms

Multiscale analysis method and experiments for the transverse mechanical property of unidirectional fiber-reinforced composites

3D printing of continuous carbon fibre reinforced polymer composites with optimised structural topology and fibre orientation

Progress in surface modification preparation, interface characterization and properties of continuous carbon fiber reinforced polymer matrix composites

Mechanical Performance and Failure Analysis of a 3D-Printed "Continuous Layer–Lattice Layer–Continuous Layer" Sandwich Structure

A multiscale study of heat treatment effects on the interlayer mechanical properties of 3D printed continuous carbon fiber‐reinforced composites

Interfacial Bonding Mechanism and Mechanical Performance of Continuous Fiber Reinforced Composites in Additive Manufacturing

Interface and performance of 3D printed continuous carbon fiber reinforced PLA composites

Experimental Characterization and Analysis of the In-Plane Elastic Properties and Interlaminar Fracture Toughness of a 3D-Printed Continuous Carbon Fiber-Reinforced Composite

3D printing for continuous fiber reinforced thermoplastic composites: mechanism and performance