Abstract:Additive manufacturing (or 3D printing) for continuous fiber composite exhibits great potential for fabrication of next-generation lightweight sophisticated structural components. Nevertheless, understanding of interface characteristics of printed parts has remained an open research question for broader applications of this new technology in engineering practice. This study aimed to evaluate the interfacial quality of 3D-printed carbon fiber reinforced plastic (CFRP) composites from two aspects: interlaminar fracture toughness in a pure mode and interfacial failure mechanism in a mixed mode. Prior to the experimental tests, the microstructural quality of the 3D printed specimens was characterized, which showed that the void content and shape of different materials are different. There is a clear boundary line where the short fiber matrix layer and the continuous fiber reinforced layer are in contact, while the interface formed between the same material layers has no evident connection traces. The standard specimens were printed for testing pure mode I and mode II interlaminar fracture toughness, through which the GCYRILLIC CAPITAL LETTER BYELORUSSIAN-UKRAINIAN IC and GIIC of interface between continuous carbon fiber layers was characterized. It was found that the fiber bridging phenomenon presented in the double cantilever beam (DCB) experiments, resulting in a higher initial mode I fracture toughness. The end notched flexure (ENF) tests found that the fracture toughness of initial mode II in between the 0 degrees continuous carbon fiber layers was relatively low. The scanning electron microscope (SEM) analysis revealed that the separated surface had only a small area of the matrix being sheared. The single lap specimen printed directly was proposed as a simplified model for simulating complex structural parts subjected to mixed stress of peel and shear. The mechanical responses and failure characteristics of the interfaces composed of different materials and different fiber angles under mixed stress were studied. It is found that each specimen presented some mixed failure modes, and the interface characteristics of different materials and different fiber orientations were completely different. The results gained in-depth understanding on the interfacial properties of 3D printing fiber reinforced structures, thereby providing key data and knowledge for practical applications.

Effect of infill density and reinforced perimeters on tensile properties and fracture mechanism of 3D printing carbon fiber–reinforced composite

Experimental and Theoretical Studies on 3D Printed Short and Continuous Carbon Fiber Hybrid Reinforced Composites

Hybrid Layout and Additive Manufacturing of Continuous Carbon/glass Fibers Reinforced Composites, and Its Effect on Mechanical Properties

Process evaluation, tensile properties, mathematical models, and fracture behavior of 3D printed continuous fiber reinforced thermoplastic composites

Effect of Infill Density, Build Direction and Heat Treatment on the Tensile Mechanical Properties of 3D-Printed Carbon-Fiber Nylon Composites

Investigation on the mechanical properties of 3D printed hybrid continuous fiber-filled composite considering influence of interfaces

Self-monitoring Continuous Carbon Fiber Reinforced Thermoplastic Based on Dual-Material Three-Dimensional Printing Integration Process

Carbon Fiber-Thermoplastic Composite 3D Printing Technology and Its Self-Monitoring

An investigation into mechanical properties of a 3D printed two-matrix continuous fiber composites with multi-cavity structure

Effect of Process Parameters on Forming Quality and Flexural Strength of Continuous Fiber Reinforced Cement-Based 3D Printed Composites

Preparation of Pre-Impregnated Continuous Carbon Fiber Reinforced Nylon6 Filaments and the Mechanical Properties of 3D Printed Composites

Layout design and mechanical behavior of 3D printed intralayer hybrid continuous carbon/glass fiber composites

Study on short fiber reinforcement mechanism for mechanical performance improvement of 3D‐printed short‐continuous carbon fiber reinforced thermoplastic composites

Experimental Study on Interface Failure Behavior of 3D Printed Continuous Fiber Reinforced Composites

Interfacial performance and fracture patterns of 3D printed continuous carbon fiber with sizing reinforced PA6 composites

Mechanical Behaviour of 3D Printed Carbon Fibre Reinforced Composite Metastructure with Various Filling Rates

Effect of Process Parameters on Tensile Mechanical Properties of 3D Printing Continuous Carbon Fiber-Reinforced PLA Composites

Effects of infill density on mechanical properties of additively manufactured chopped carbon fiber reinforced PLA composites

Effects of FDM-3D printing parameters on mechanical properties and microstructure of CF/PEEK and GF/PEEK

Effect of process parameters on properties of 3D printed continuous fiber reinforced thermoplastic composites

Effects of Infill Characteristics and Strain Rate on the Deformation and Failure Properties of Additively Manufactured Polyamide-Based Composite Structures