Tribological Behavior of Polydiethylsiloxane (PDES) in a Si3N4 and M50 System under Low Temperatures from −80 to 25 °C
Junhao Han,Yong Tang,Luo Yue,Xianzhen Ma,Hao Jia,Ningxia Liu,Pengpeng Bai,Yonggang Meng,Yu Tian
DOI: https://doi.org/10.3390/lubricants12050176
2024-01-01
Lubricants
Abstract:Lubricants must exhibit good tribological behavior at low temperatures to ensure reliable startups in very cold regions. This study investigates the performance of lubricants, with a specific focus on their capacity for high-temperature lubrication and ensuring reliable low-temperature startup in engines. Experiments were conducted to assess the friction and wear characteristics of polydiethylsiloxane in conjunction with a Si3N4 ball and M50 (8Cr4Mo4V) steel across a temperature range of −80 °C to 25 °C. The results indicate that the coefficient of friction, as determined through friction and wear tests at various temperatures, remained below 0.1. As temperatures progressively decreased, the system’s friction coefficient increased, and wear volumes recorded at 25 °C and −60 °C were 9749.513 µm³ and 105.006 µm³, respectively, culminating in lubrication failure at −100 °C. This failure is primarily attributed to the increased viscosity and decreased mobility of polydiethylsiloxane at extremely low temperatures. Additionally, the reduced temperature increases the strength of the quenched steel, leading to hard particles or protrusions on the material’s surface, which collide with the Si3N4 ball during friction, causing adhesion and spalling. Despite this, polydiethylsiloxane forms a stable protective oil film on the surface, enhancing the system’s lubrication performance. However, below −80 °C, this oil film begins to tear, leading to diminished lubrication efficacy. This study provides valuable data supporting the field of cryogenic lubrication.