3Li2S-2MoS2 filled composite polymer PVDF-HFP/LiODFB electrolyte with excellent interface performance for lithium metal batteries

Sheng-Dong Tao,Jian Li,Rong Hu,Lihua Wang,Zhexi Chi,Tengfei Li
DOI: https://doi.org/10.1016/j.apsusc.2020.147794
IF: 6.7
2021-01-01
Applied Surface Science
Abstract:<p>Solid polymer electrolytes (SPEs) are close to commercialization owing to their high flexibility, low cost, and easy processing. However, the further commercial applications of SPE are hindered by low ionic conductivity and poor mechanical properties. To solve the problems, a porous and intercalated 3Li<sub>2</sub>S-2MoS<sub>2</sub> (LMS) was prepared as an active filler. LMS and lithium oxalyldifluroborate (LiODFB) were embedded with the poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) in a composite intercalated solid polymer electrolyte (CSE-LMS). The CSE-LMS exhibits excellent properties such as high ionic conductivity (2.51 × 10<sup>-4</sup> S·cm<sup>−1</sup> at 60 ℃) with a favorable stability electrochemical window of 4.8 V (vs. Li/Li<sup>+</sup>), superior interface stability with lithium metal and outstanding mechanical strength. The LiCoO<sub>2</sub>/CSE-LMS/Li cell was assembled to construct a high specific energy device, which delivered excellent C-rate performance and a specific capacity of 145.79 mA·h·g<sup>−1</sup> with a capacity retention of &gt; 86.22% after 200 cycles at 0.5C. The LMS reduces polymer crystallinity and stablizes the interface conformation achieved by LMS interacting with PVDF-HFP and LiODFB. The results suggest that CSE-LMS12 doped with 12 wt% LMS is a promising SPE for solid-state batteries.</p>
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films
What problem does this paper attempt to address?
The problems that this paper attempts to solve mainly focus on several key issues existing in solid - state polymer electrolytes (SPEs) used in solid - state lithium - metal batteries (SLBs): 1. **Low ionic conductivity**: The ionic conductivity of traditional SPEs at room temperature is low (usually less than \(10^{-5} \, \text{S·cm}^{-1}\)), which limits their practical applications. The paper improves the ionic conductivity of SPEs by introducing the active filler 3Li\(_2\)S - 2MoS\(_2\) (LMS). 2. **Poor mechanical properties**: The mechanical strength of SPEs is weak, which easily leads to the formation of lithium dendrites, thus affecting the safety and cycle life of the battery. By embedding LMS into the PVDF - HFP matrix, the paper improves the mechanical strength of the composite solid - state polymer electrolyte (CSE - LMS) and effectively suppresses the growth of lithium dendrites. 3. **Poor interface stability**: The interface stability between SPEs and the lithium - metal anode is poor, which easily leads to an increase in interface impedance and affects the performance of the battery. Through the synergy of LMS with PVDF - HFP and LiODFB, the paper stabilizes the interface structure and reduces the interface impedance. 4. **Narrow electrochemical window**: The electrochemical window of SPEs is narrow, which limits the application of high - voltage cathode materials. The CSE - LMS in the paper has a wider electrochemical window (4.8 V vs. Li\(^+\)/Li), which is suitable for the use of high - voltage cathode materials. 5. **High crystallinity**: The high crystallinity of the PVDF - HFP matrix is not conducive to the transport of lithium ions. The addition of LMS reduces the crystallinity of PVDF - HFP, increases the amorphous region, and thus improves the transport rate of lithium ions. In summary, by designing and preparing a new type of composite solid - state polymer electrolyte CSE - LMS, this paper aims to solve the problems of low ionic conductivity, poor mechanical properties, poor interface stability, narrow electrochemical window, and high crystallinity encountered by SPEs in practical applications, so as to improve the overall performance of solid - state lithium - metal batteries.