Abstract:The microstructural features and hardness of He-irradiated miscible Cu/Zr crystalline/crystalline nanolaminates with a negative enthalpy of mixing were investigated at room temperature. The distribution of He bubbles within the Cu layers exhibits a high dependence on both layer thickness (h) and ion dose (Phi), while that at the Cu-Zr interfaces is only affected by ion dose. Compared with their as-deposited counterparts, the He-irradiated Cu/Zr nanolaminates tend to manifest radiation-induced solid-state amorphization (RSA), which was induced by ion beam mixing and initiated from crystalline interfaces. The size-dependent hardness of the as-deposited Cu/Zr nanolaminates is elucidated by a transition in the strengthening mechanism from the interfacial barrier strengthening mechanism to the confined layer slip of partials when h is increased. In the He-irradiated Cu/Zr samples, however, the size-dependent hardness is highly related to Phi. Under lower Phi, a nonmonotonically h dependent irradiation hardening is evident and is associated with a transition from irradiation hardening at large h (>= 10 nm) to softening at small h (< 10 nm), and the maximum hardening occurs at a critical value of h approximate to 25 nm. In contrast, under higher Phi , the Cu/Zr nanolaminates merely display irradiation softening behavior, with the minimum softening at the critical value of h approximate to 25 nm. The underlying mechanisms are highlighted in terms of dislocation-bubble interactions and RSA. These findings indicate the effects of He ion dose and layer thickness on the He bubble distribution and the interface-mixing of Cu/Zr nanolaminates as well as provide thorough insight into how to tune the He ion dose to manipulate the mechanical response of nanolaminated FCC/HCP materials on a small scale.

Morphological changes, He desorption behaviors, and He bubble evolution of He-charged Cu films prepared by DC magnetron sputtering during annealing

Investigation on Thermal Release Behavior of Helium-Charged Copper Films by Dc Magnetron Sputtering

Effect of He Content on Microstructure, Mechanical Properties and He Thermal Desorption Behavior of W Film Fabricated by RF Magnetron Sputtering

EFFECT OF ANNEALING ON THE CuInS2 THIN FILMS PREPARED BY CHEMICAL BATH DEPOSITION

The Effect of Thermal Annealing of Mo Film on the CuInSe2 Layer Texture and Device Performance

Effects of Annealing on Structural and Electrical Properties of CuInSe 2 Thin Films Prepared by Hybrid Sputtering/Evaporation Processes

Diluting and Annealing Effects on Electromigration and Morphology of Chemical Vapor-Deposited Copper Films

The Effect of Thermal Annealing on the Microstructure and Mechanical Properties of Magnetron Sputtered Hydrogenated Amorphous Carbon Films

Molecular dynamics investigation of deposition and annealing behaviors of Cu atoms onto Cu(0 0 1) substrate

Effect of Thermal Treatment on the Mechanical Properties of Cu Specimen Fabricated Using Electrodeposition Bath for Through-Silicon-via Filling

Molecular dynamics investigation of deposition and annealing behaviors of Cu atoms onto Cu(001) substrate

Thermal Annealing Behavior of Helium in Ti Films Deposited by Magnetron Sputtering

Effects of Annealing at Ar Ambient on the Physical Properties of Zn0.66Co0.34O Thin Film

Size- and Ion-Dose-dependent Microstructural Evolution and Hardening in He-irradiated Miscible Cu/Zr Crystalline/crystalline Nanolaminates

Barrier layer and annealing temperature dependent microstructure evolution of nanocrystalline Cu films

Effect of Annealing Ambient on the Thermal Stability of Cu/Zr42si9n49/Si Contact System

Evolution Of The Magnetization Depth Profile Of Fe/Cu(100) Films Upon Thermal Annealing

Microstructure and mechanical property evolution of He-implanted nanochannel W film under post-annealing

Annealing effect on morphology and magnetism of ultrathin films of Fe and Ni on Cu(100)

Effect of Thermal Annealing on Phase Structure and Hydrogen Evolution Reaction of Molybdenum Carbide Thin Films Prepared by Co-Sputtering

Annealing Improved Ductility and Fracture Toughness of Nanocrystalline Cu Films on Flexible Substrates