Insight into High Temperature Gas-Phase Arsenic Capture by a CaO–Ca 12 Al 14 O 33 Synthetic Sorbent

Zhongli He,Bing Song,Cai Liang,Bin Liu,Zhirui Ma,Keliang Pang,Jiangang Yang

DOI: https://doi.org/10.1021/acs.energyfuels.0c03686

2021-01-19

Abstract:Concerns about arsenic emission issues are growing as the arsenic discharged from coal-fired power plants seriously endangers the ecological environment and public health. The gas-phase arsenic capture by a CaO–Ca₁₂Al₁₄O₃₃ synthetic sorbent at 1000–1200 °C in the simulated flue gas was conducted, with the influence of the addition ratio of Ca₁₂Al₁₄O₃₃, temperature, retention time, and acid gases NO/SO₂ considered in the study. The results indicated that the synthetic sorbent containing 15 wt % Ca₁₂Al₁₄O₃₃ (Ca85Al15) exhibited much better arsenic adsorption performance than CaO, which was ascribed to the greatly strengthened sintering resistance of CaO particles by adding Ca₁₂Al₁₄O₃₃, enabling arsenic adsorption and chemical reactions. Both the increasing temperature and retention time facilitated arsenic adsorption by Ca85Al15, and the hypertoxic arsenic vapor (As³⁺) was converted into arsenate (Ca₃(AsO₄)₂) with less toxicity. In the presence of NO, the arsenic capture was gradually suppressed with increasing retention time. On the other hand, SO₂ could slightly facilitate the capture of arsenic at 1000–1100 °C for 10 min; nevertheless, due to the formation of Ca₄Al₆O₁₂SO₄, the promotion effect was inhibited at a higher temperature and a longer retention time. In general, the study provided a basis for developing highly efficient solid sorbents toward controlling arsenic vapor emission derived from coal combustion, and the appropriate conditions for arsenic capture were at 1000–1100 °C.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.0c03686?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.0c03686</a>.Schematic illustration of the preparation procedure to synthesize CaO–Ca₁₂Al₁₄O₃₃ (Figure S1) and diagrams of the adsorption–desorption isotherms of Ca85Al15 and pore-size distribution curves of CaO and synthetic sorbents with different CaO/Ca₁₂Al₁₄O₃₃ ratios based on BJH adsorption data (Figure S2) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.0c03686/suppl_file/ef0c03686_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

energy & fuels,engineering, chemical