Abstract:For the first time, a nanosheet-state CoMnx mixed oxide with multifarious active regions was synthesized by oxidation-etching assembly of metal organic framework (MOF) precursor and applied for catalytic combustion of toluene at low temperatures. The obtained optimum catalyst denoted as CoMn6 showed excellent performance, which achieved 90% conversion of 1,000 ppm toluene under a weight hourly space velocity (WHSV) of 60,000 mL/(g·h) at 219 °C. While, it also exhibited long-term stability with strong water resistance property. The characterizations of physicochemical properties indicated that the oxidation-etching assembly process built an abundant mesoporous structure in the CoMnx catalyst, which greatly increased the specific surface area (SSA). Especially, potassium permanganate as oxidant and manganese source led to uniform dispersion and assembling of cobalt atoms, which caused the generation of low-crystallinity CoMnx mixed oxide with abundant dislocations, vacancies, phase interfaces and amorphous structures, resulting in excellent low-temperature reducibility, outstanding lattice oxygen mobility and abundant active species such as Mn 3+ , Co 3+ and adsorbed oxygen species. Density functional theory (DFT) calculations demonstrated that gaseous oxygen with the longer bond length (1.406 Å) and stronger adsorption energy (−4.443 eV) could be adsorbed and activated well on the MnCo 2 O 4.5 (3 1 1) plane, which is beneficial for the toluene oxidation. In situ diffuse reflectance infrared spectroscopy (DRIFTS) technique was applied to track the intermediates of toluene combustion under different atmospheres, which further deduced the contributions of different active regions and oxidation mechanism over the CoMnx catalyst. The present facile strategy of oxidation-etching assembly of the MOF precursor for the creating of novel catalyst with high performance could be applied in a wide variety of materials besides VOC combustion catalysts.

Rational Design and Construction of Monolithic Ordered Mesoporous Co 3 O 4 @SiO 2 Catalyst by a Novel 3D Printed Technology for Catalytic Oxidation of Toluene

A novel 3D printed technology to construct a monolithic ultrathin nanosheets Co3O4/SiO2 catalyst for benzene catalytic combustion

Direct ink writing of Pd-Decorated Al<sub>2</sub>O<sub>3</sub> ceramic based catalytic reduction continuous flow reactor

Enhancing Oxygen Activation Ability by Composite Interface Construction over a 2D Co3O4-Based Monolithic Catalyst for Toluene Oxidation

Self-assembly of a Highly Stable and Active Co3O4/H-TiO2 Bulk Heterojunction with High-Energy Interfacial Structures for Low Temperature CO Catalytic Oxidation

Tailored monolithic catalyst and reactor by direct photo-curing 3D printing for oxidative desulfurization of fuels

Structure and Catalytic Activity of 3D Macro/mesoporous Co3O4 for CO Oxidation Prepared by a Facile Self-Sustained Decomposition of Metal–organic Complexes

Stereolithography 3D printed monolithic catalyst for highly efficient oxidative desulfurization of fuels

Fabrication of Three-Dimensional Ordered Mesoporous Manganese Oxides Used As High-Efficient Catalysts for Removal of Toluene and Carbon Monoxide

3D Printing of Hierarchically Porous Monolithic Ts‐1 Catalyst for One-Pot Synthesis of Ethylene Glycol

Fabrication of High-performance CeO2-MnOx/TiO2/Ti Monolithic Catalysts for Low-temperature and Stable CO Oxidation

Engineering Co3O4@3DOM LaCoO3 multistage-pore nanoreactor with superior SO2 resistance for toluene catalytic combustion

One-step synthesis of three-dimensional mesoporous Co3O4@Al2O3 nanocomposites with deep eutectic solvent: An efficient and stable peroxymonosulfate activator for organic pollutant degradations

Three-dimensional mesoporous manganese oxides and cobalt oxides: High-efficiency catalysts for the removal of toluene and carbon monoxide

Coaxial 3D Printing of Zeolite-Based Core-Shell Monolithic Cu-SSZ-13@SiO2 Catalysts for Diesel Exhaust Treatment

Efficient Noble-Metal-Free Catalysts Supported by Three-Dimensional Ordered Hierarchical Porous Carbon.

Hierarchical laminated Al2O3 in-situ integrated with high-dispersed Co3O4 for improved toluene catalytic combustion

CuO/TiO 2 /Ti Monolithic Catalysts for Low-Temperature CO Oxidation

Nanosheet-state cobalt-manganese oxide with multifarious active regions derived from oxidation-etching of metal organic framework precursor for catalytic combustion of toluene

A metal–organic framework route to in situ encapsulation of Co@Co3O4@C core@bishell nanoparticles into a highly ordered porous carbon matrix for oxygen reduction

Direct Vat‐Photopolymerization 3D Printing of Hierarchically Porous SiC Loaded with Co/Ni Based Catalysts by Using Pickering Emulsions