Haiyong Liu,Yajie Feng,Yirong Yao,Bingsheng Li,Renda Wang,Xiaoguang Shi,Peng Li,Jie Shu,Feng Huang,Qing Huang,Fangfang Ge
Abstract:<p>Cr-coated Zirlo tubes were conducted in the autoclave corrosion (345 °C and 16.5 MPa), followed by the 1200 °C steam oxidation. After the 1-h oxidation, the coated tubes exhibited structural integrity, in contrast to the uncoated ones that had broken into pieces. Moreover, the coated tubes that already underwent the 45-days pre-corrosion, still remained good oxidation resistance with the weight gain of ∼4.46 mg/cm<sup>2</sup>. During the pre-corrosion, very thin Cr<sub>2</sub>O<sub>3</sub> tissue formed on the outmost surface and along the columnar boundaries, which would suppress the formation of bubbles and cracks in the subsequent oxidation.</p>
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the high - temperature steam oxidation behavior and corrosion resistance of chromium - coated zirconium alloy cladding tubes after long - term supercritical water corrosion in a high - temperature and high - pressure steam environment. Specifically, the research focuses on the following aspects:
1. **Improving the accident tolerance of zirconium alloy cladding materials**: Zirconium alloys are widely used as cladding materials in nuclear reactors due to their low neutron absorption rate, high radiation damage resistance, and good mechanical properties. However, in the case of cooling water failure, zirconium alloys are prone to react violently with high - temperature steam, releasing a large amount of explosive hydrogen gas and heat, as shown in the Fukushima nuclear power plant accident. Therefore, it is very important to enhance the tolerance of zirconium alloy cladding materials under accident conditions.
2. **Evaluating the impact of pre - corrosion on the chromium coating**: Most previous studies have mainly focused on the protection ability of the chromium coating under a single environmental factor (such as supercritical water or high - temperature steam). However, from a practical application perspective, cladding materials usually may encounter accident conditions (high - temperature steam oxidation) only after long - term corrosion in supercritical water (300 - 400°C, 10 - 20 MPa). Therefore, it is very necessary to understand the oxidation resistance of the chromium coating that has already undergone long - term supercritical water corrosion in high - temperature steam.
3. **Experimental design and result analysis**: To study this problem, the author conducted the following experiments:
- Chromium - coated and uncoated zirconium alloy tubes were immersed in supercritical water at 345°C and 16.5 MPa for 15 days and 45 days respectively.
- Subsequently, these samples were subjected to a 1 - hour oxidation test in high - temperature steam at 1200°C.
- Compare the oxidation resistance and microstructure changes of samples under different treatment conditions.
Through these experiments, the author hopes to verify whether the chromium coating can still maintain good high - temperature steam oxidation resistance after long - term supercritical water corrosion, and explore the specific impact of pre - corrosion on the oxidation behavior of the chromium coating.
### Main findings
- **Protection effect of the chromium coating**: After 15 - day and 45 - day supercritical water corrosion, the chromium - coated zirconium alloy tubes still showed good oxidation resistance, with a weight gain of only about 4.46 mg/cm², while the uncoated zirconium alloy tubes had broken into fragments under the same conditions.
- **Impact of pre - corrosion**: During the pre - corrosion process, a very thin Cr₂O₃ layer was formed on the surface of the chromium coating, and Cr₂O₃ structures were filled along the columnar boundaries, which helped to inhibit the formation of bubbles and cracks in the subsequent oxidation process, thereby improving the antioxidant performance of the coating.
### Conclusion
This research shows that the chromium coating can still effectively prevent the oxidation of the zirconium alloy substrate in high - temperature steam after long - term supercritical water corrosion, which provides an important basis for the practical application of the chromium coating in nuclear reactor cladding materials.