Abstract:Coating technology to modify the property of zirconium (Zr) alloy is a potential method for accident-tolerant fuel claddings. In this work, Cr-coated and CrN-coated are prepared on the surface of Zr alloy by using multi-arc ion plating technology. The effect of coatings on the high-temperature oxidation performance at 800, 1000, and 1200 °C has been investigated. The oxidation behavior, microstructure, and phase composition of the samples were characterized by scanning electron microscopy, atomic force microscope and X-ray diffraction analysis. The mechanical properties of the coatings before and after oxidation were examined by ring compressive and hardness tests. It is shown that all the Cr and CrN coating can effectively protect the substrate from oxidation corrosion in air due to the formation of Cr2O3, which can effectively reduce the penetration of oxygen. The thickness of the oxide layer from the side of the coating doesn't exceed to 5 μm at 1000 °C, and from the uncoated side reaches to 70 μm with pores and rough structure. Bubbles appeared on the surface of the coated samples after oxidizing at 1200°C. These bubbles are located at the Cr and Cr2O3 layers. The high-temperature oxidation resistance of Cr coating at 1200°C is better than that of CrN, the latter appears to crack and spall on the oxide layer. Due to the higher fracture toughness, ductility of the Cr coating and more suitable deformation compatibility, the Cr coating possesses better crack resistance than the CrN coating under mechanical loading.

Fiber texture-dependent oxidation behaviour of Cr-coated zirconium alloy in high temperature steam

Evolution of Cr/Cr2O3 interface in Cr-coated zirconium alloy in high temperature steam

Systematic investigations on the oxidation mechanism of Cr coated Zr-4 alloy under different high-temperature steam conditions

Microstructure Evolution and Failure Mechanism of Cr-coated Zry-4 in Air and Steam at 1200 °C

Investigations on 1200 °C steam oxidation behavior of Cr coatings with distinct crystallographic orientation on Zircaloy-4 alloys

Oxidation Behavior of Cr-coated Zirconium Alloy Cladding in High-Temperature Steam above 1200 °C

Insights into 1200 °C steam oxidation behavior of Cr coatings with different microstructure on Zircaloy-4 alloys for enhanced accident tolerant fuel cladding

Tem Characterizations of a Zro2/Cr Composite Coating on Zr-1nb Alloy after 1200°C Steam Oxidation

The high-temperature oxidation and mechanical properties of the Cr/Zr and CrN/Zr coating

Oxidation behavior, thermal stability, and the coating/substrate interface evolution of CrN-coated Zircaloy under high-temperature steam

Mechanical and high-temperature steam oxidation properties of Cr coatings deposited via high-power impulse magnetron sputtering

Improved oxidation resistance of Cr/FeCrAl coating on Zr alloy in high-temperature steam environment

Enhancing the oxidation behaviors of Zr alloys for nuclear fuel cladding using nanolamellar Cr/CrN coating

High-Temperature Oxidation And Tensile Behaviors Of Cral Coating On Zirconium Alloy

Effect of Diffusion Barriers on Steam Oxidation Properties and Interface Evolutions of Cr Coating for Zirconium Alloy at 1200 °C

Reducing the Oxidation Rate of Cr-coated Zr Alloys under High Temperature Steam Environment: an Approach of an Outer Zr Coating

Steam oxidation of Cr-coated zirconium alloy claddings at 1200 °C: Kinetics transition and failure mechanism of Cr coatings

Construction of chromium coatings with (200) preferred orientation and exploration the high-temperature steam oxidation properties

Isothermal experiments on steam oxidation of magnetron-sputtered chromium-coated zirconium alloy cladding at 1200 °C

Improvement of the high-temperature steam oxidation resistance of Zirlo tubes by multilayer Cr/CrAlSiN coatings

Long‐term high‐temperature steam oxidation behavior of Cr‐coated Zircaloy‐4 alloy for accident tolerant fuel