Abstract:In this work, transparent cellulose aerogels are produced from non‐modified microcrystalline cellulose in an approach, which utilizes only salts, water, ethanol and CO2. Ca2+‐cross‐linking of cellulose molecule chains facilitates a high degree of microstructural control. The resulting products exhibit specific surface areas higher than 600 m2 g and light transmittance of up to 91% at substrate thicknesses in the millimeter range. In this work, nanostructured and transparent cellulose aerogels are synthesized via a purely salt induced approach from non‐modified microcrystalline cellulose type II. The production process requires in contrast to state of the art methods no pretreatment of cellulose or use of expensive cellulose‐solvents: it consists of hydrogel formation via cross‐linking of cellulose with calcium ions, a solvent exchange and a supercritical drying step. A systematic multiparameter study reveals that a high level of structural control is achievable: ratios of macro‐ to mesoporosity and the size of mesopores can be tailored by adjustment of the calcium ion content, while keeping a high overall porosity in the range of 92% – 96 %. The build‐up of homogeneous, fine pore structures results in a significant increase of the specific surface area as compared to conventional calcium‐free aerogels (684 vs. 300 m2 g−1). Remarkably, the Ca2+‐cross‐linking renders aerogels transparent, with Rayleigh scattering being the dominant scattering mechanism. Additional ion exchange to Ca2+ in the hydrogel‐state leads to further reduction of the pore size and to products with optimized optical properties, e.g., light transmission of 91% at an incidents light wavelength of 800 nm and a substrate thickness of 1.5 mm.

Cellulose Ester-Based Aerogel: Lightweight and Highly Water-Absorbent

Fabrication of Cellulose Aerogel from Wheat Straw with Strong Absorptive Capacity

Recycling of an Agricultural Bio-waste as a Novel Cellulose Aerogel: A Green Chemistry Study

Cellulose Aerogels from Aqueous Alkali Hydroxide–Urea Solution

Cellulose Aerogels from Paper Waste for Excellent Oil Spill Cleaning and Heat Insulation

Bacterial cellulose composite aerogel with high elasticity and adjustable wettability for dye absorption and oil–water separation

Fabrication of Cellulose Aerogels Using a Green/Clean Procedure

Green Strong Cornstalk Rind-Based Cellulose-PVA Aerogel for Oil Adsorption and Thermal Insulation

Cellulose Aerogels: Synthesis, Applications, and Prospects

Cellulose Aerogels Prepared from Cellulose/amimcl Solutions

Porous Cellulose Aerogels with High Mechanical Performance and Their Absorption Behaviors

Cellulose aerogels prepared from an aqueous zinc chloride salt hydrate melt

Transparent Cellulose Aerogels from Concentrated Salt Solutions: Synthesis and Characterization

Highly Compressible, Anisotropic Aerogel with Aligned Cellulose Nanofibers

Aerogel from sustainably grown bacterial cellulose pellicle as thermally insulative film for building envelope

Feasibility for the preparation of aerogels with celluloses extracted mildly from waste palm leaves

Preparation of mechanically strong and lightweight cellulose aerogels from cellulose-NaOH/PEG solution

An Efficient and Economic Approach for Producing Nanocellulose-Based Aerogel from Kapok Fiber

Mechanical Properties of Cellulose Aerogel Composites with and without Crude Oil Filling

Preparation and characterization of cellulose/attapulgite composite aerogels with high strength and hydrophobicity

Anisotropic cellulose nanofiber/chitosan aerogel with thermal management and oil absorption properties