Abstract:Cu matrix composites have received increased attention in a wide industrial area because of their excellent mechanical properties and good electrical and thermal conductivity. However, the addition of general ceramic reinforcements often leads to a marked reduction in electrical conductivity for Cu matrix composites. In this study, the ZrB 2 -reinforced Cu composites have been developed to overcome this drawback since these metal borides possess relatively high electrical conductivity. The 5 wt.% ZrB 2 /Cu composites were prepared using hot-pressed sintering techniques at varying temperatures from 760 to 920°C. The influence of sintering temperature on the microstructure, relative density, and mechanical and electrical properties was examined. The results of the SEM observation show that ZrB 2 particles are seamlessly integrated into the Cu matrix for all ZrB 2 /Cu composites. The average grain size of the Cu matrix increases from 360 to 980 nm with the increase of the sintering temperature. The increase in sintering temperature also leads to the surface porosity decrease from 1.4 to 0.4%. The relative density and electric conductivity of the composites increase at the same time as the sintering temperature increases. However, microhardness increases and decreases, with a maximum value of 92 HV0.2 achieved at 840°C. The elastic modulus and nanohardness maps determined from the nanoindentation indicate that the reinforced ZrB 2 particles demonstrate the highest values for elastic modulus (340–500 GPa) and nanohardness (30–48 GPa). At the same time, the Cu matrix possesses a modulus of 100–200 GPa and nanohardness of about 10 GPa. TEM observation confirmed that the sintering temperature exhibits little influence on the interface reaction between ZrB 2 and Cu. Both sharp interface and interface with amorphous transition layer are observed. The variation of microhardness is mainly due to the strengthening of grain refinement and to the mismatch of the thermal expansion coefficients. The above results can provide further insights into the deeper understanding of the role of sintering temperature during hot-pressed sintering.

Sintering pressure effect on the performances of near-zero thermal expansion xLFCS/Cu metal matrix composites

Process optimization, microstructures and mechanical/thermal properties of Cu/Invar bi-metal matrix composites fabricated by spark plasma sintering

Design of near-zero thermal expansion composites with superior mechanical properties in a wide temperature region

Lightweight and near-zero thermal expansion ZrW2O8-SiCnw/Al hybrid composites

Near-zero thermal expansion of ZrW2O8/Al–Si composites with three dimensional interpenetrating network structure

ZrW2O8/ZrO2 Composites with Low/Near-Zero Coefficients of Thermal Expansion Fabricated at Ultralow Temperature: an Integration of Hydrothermal Assembly and a Cold Sintering Process

Adjustable Thermal Expansion in La( Fe, Si)(13)-based Conductive Composites by High-Pressure Synthesis

The effect of interface reaction on the thermal and mechanical properties of Mn3.2Zn0.5Sn0.3N/Al composites

Effects of Zr-Cu Alloy Powder on Microstructure and Properties of Cu Matrix Composite with Highly-Aligned Flake Graphite

Realization of high thermal conductivity and tunable thermal expansion in the ScF3@Cu core-shell composites

Effect of Sintering Temperature on the Microstructure and Properties of High-Strength and Highly Conductive 5 wt.% ZrB2/Cu Composite

Enhanced shear strength and microstructure of Cu–Cu interconnection by low-temperature sintering of Cu nanoparticles

Isotropic Negative Thermal Expansion in the Multiple-Phase La-Fe-Co-Si-Cu Alloys with Enhanced Strength and Ductility

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Optimisation of the spark plasma sintering process for high volume fraction SiCp/Al composites by orthogonal experimental design

Evaluation of tribo-mechanical measurements and thermal expansion of Cu-based nanocomposites reinforced by high strength hybrid ceramics

Design of negative/nearly zero thermal expansion behavior over a wide temperature range by multi-phase composite

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures

A zero-thermal-expansion composite with enhanced thermal and electrical conductivities resulting from 3D interpenetrating copper network

Matrix-filler interfaces and physical properties of metal matrix composites with negative thermal expansion manganese nitride

Pressure Effects on a Novel W-Mo-Cu Alloy by Large Current Electric Field Sintering: Sintering Behavior, Microstructure and Properties