Investigation on the corrosion resistance of the CuO-Al2O3 composite coating prepared by micro-arc oxidation

Dong-dong Wang,Xin-tong Liu,Qing Zhang,Qing-wen Li,Han Chen,Yan Wang,Da-long Li,De-jiu Shen

DOI: https://doi.org/10.1016/j.matlet.2021.129396

IF: 3

2021-04-01

Materials Letters

Abstract:A CuO-Al2O3 composite coating was obtained by an AC deposition and a followed secondary MAO treatment in an acidic copper sulfate electrolyte and an alkaline sodium hexametaphosphate electrolyte. Analyzes on phase and elemental composition and microstructure showed that a continuous CuO layer was formed on the top of the original MAO coating. EIS test suggested that after a secondary MAO treatment for 1 min, the samples obtained by AC deposition for 5 min had the best corrosion resistance, because of the barrier of CuO layer to the NaCl solution.

materials science, multidisciplinary,physics, applied

What problem does this paper attempt to address?

The problem this paper attempts to address is improving the corrosion resistance of micro-arc oxidation (MAO) coatings. Specifically, the authors formed a continuous CuO layer on the original MAO coating through alternating current (AC) deposition and secondary micro-arc oxidation treatment to enhance the coating's corrosion resistance. The study found that after 5 minutes of AC deposition and 1 minute of secondary micro-arc oxidation treatment, the sample exhibited the best corrosion resistance because the CuO layer effectively blocked the NaCl solution from penetrating the coating.

### Main Research Content:
1. **Coating Preparation Method**:
- Depositing Cu on the MAO coating using AC deposition.
- Subsequently performing secondary micro-arc oxidation treatment to convert the deposited Cu into CuO.

2. **Coating Characterization**:
- Analyzing the phase composition of the coating through X-ray diffraction (XRD).
- Using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) to analyze the microstructure and elemental distribution of the coating.
- Testing the corrosion resistance of the coating through electrochemical impedance spectroscopy (EIS).

3. **Experimental Results**:
- After 5 minutes of AC deposition, Cu deposition spots formed on the surface of the MAO coating, which disappeared after secondary micro-arc oxidation treatment, forming a layer of CuO nanoparticles.
- EIS test results showed that the sample (D5M) with 5 minutes of AC deposition and 1 minute of secondary micro-arc oxidation treatment had the best corrosion resistance.

### Conclusion:
Forming a continuous CuO layer on the MAO coating can significantly improve the coating's corrosion resistance. In particular, the sample (D5M) with 5 minutes of AC deposition and 1 minute of secondary micro-arc oxidation treatment exhibited the best corrosion resistance. This is because the CuO layer can effectively block the corrosive medium from entering the coating, thereby enhancing the overall corrosion resistance.